Thermodynamics of Boron Removal from Silicon Using CaO-MgO-Al2O3-SiO2 Slags

被引：11
|
作者：
Jakobsson, Lars Klemet [1 ]
Tangstad, Merete [2 ]
机构：
[1] Elkem Technol, Fiskaaveien 100, N-4675 Kristiansand, Norway
[2] NTNU Norwegian Univ Sci & Technol, Dept Mat Sci & Engn, Hogskoleringen 1, N-7491 Trondheim, Norway
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2018年 / 49卷 / 04期
关键词：
MOLTEN SILICON; CALCIUM; SYSTEM;
D O I：
10.1007/s11663-018-1250-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Slag refining is one of few metallurgical methods for removal of boron from silicon. It is important to know the thermodynamic properties of boron in slags to understand the refining process. The relation of the distribution coefficient of boron to the activity of silica, partial pressure of oxygen, and capacity of slags for boron oxide was investigated. The link between these parameters explains why the distribution coefficient of boron does not change much with changing slag composition. In addition, the thermodynamic properties of dilute boron oxide in CaO-MgO-Al2O3-SiO2 slags was determined. The ratio of the activity coefficient of boron oxide and silica was found to be the most important parameter for understanding changes in the distribution coefficient of boron for different slags. Finally, the relation between the activity coefficient of boron oxide and slag structure was investigated. It was found that the structure can explain how the distribution coefficient of boron changes depending on slag composition.
引用
收藏
页码：1699 / 1708
页数：10
相关论文
共 50 条
  • [41] Influence of Al2O3 and MgO on the Viscosity and Stability of CaO-MgO-SiO2-Al2O3 Slags with CaO/SiO2=1.0
    Sun, Chang-yu
    Liu, Xiao-hong
    Li, Jing
    Yin, Xi-tao
    Song, Sunny
    Wang, Qi
    [J]. ISIJ INTERNATIONAL, 2017, 57 (06) : 978 - 982
  • [42] Sulphide capacities of CaO-SiO2-Al2O3-MgO slags
    Hayakawa, H
    Hasegawa, M
    Oh-nuki, K
    Sawai, T
    Iwase, M
    [J]. STEEL RESEARCH INTERNATIONAL, 2006, 77 (01) : 14 - 20
  • [43] CRYSTALLIZATION KINETICS OF CaO-SiO2-Al2O3-MgO SLAGS
    Esfahani, Shaghayegh
    Barati, Mansoor
    [J]. ADVANCES IN MOLTEN SLAGS, FLUXES, AND SALTS, 2016, : 237 - 244
  • [44] VISCOSITY OF SYNTHETIC CAO-MGO-SIO2-AL2O3 SLAGS
    ZILBER, MK
    [J]. RUSSIAN METALLURGY-METALLY-USSR, 1967, (04): : 18 - &
  • [45] Melting experiments in the systems CaO-MgO-Al2O3-SiO2 and MgO-SiO2 at 3 to 15 GPa
    Herzberg, C
    Zhang, JZ
    [J]. AMERICAN MINERALOGIST, 1998, 83 (5-6) : 491 - 500
  • [46] ON THE VISCOSITY OF SLAGS OF THE CAO-MGO-SIO2-AL2O3 SYSTEM
    ZYATKOVA, LR
    MILLER, SN
    [J]. RUSSIAN METALLURGY, 1981, (03): : 27 - 29
  • [47] Viscosities of the Quaternary Al2O3-CaO-MgO-SiO2 Slags
    Song, Minho
    Shu, Qifeng
    Du Sichen
    [J]. STEEL RESEARCH INTERNATIONAL, 2011, 82 (03) : 260 - 268
  • [48] Viscosity of CaO-SiO2-Al2O3-MgO-B2O3 slags
    Babenko A.A.
    Istomin S.A.
    Protopopov E.V.
    Sychev A.V.
    Ryabov V.V.
    [J]. Steel in Translation, 2014, 44 (2) : 110 - 112
  • [49] REDOX EQUILIBRIA IN AL2O3-CAO-FEOX-SIO2 AND AL2O3-CAO-FEOX-MGO-SIO2 SLAGS
    JAHANSHAHI, S
    WRIGHT, S
    [J]. ISIJ INTERNATIONAL, 1993, 33 (01) : 195 - 203
  • [50] SULFUR DISTRIBUTION BETWEEN LIQUID-IRON AND CAO-MGO-AL2O3-SIO2 SLAGS USED FOR LADLE REFINING
    TSAO, T
    KATAYAMA, HG
    [J]. TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 26 (08) : 717 - 723
12345