Fatigue damage and fatigue life diagrams of a carbon/epoxy cross ply laminate aged by hygrothermal exposure

被引：12

作者：

Pereira Fulco, Ana Paula ^{[1
]}

de Medeiros, Antonio Marcos ^{[1
]}

Passaia Tonatto, Maikson Luiz ^{[2
]}

Amico, Sandro Campos ^{[3
]}

Talreja, Ramesh ^{[4
]}

Diniz Melo, Jose Daniel ^{[1
]}

机构：

[1] Univ Fed Rio Grande do Norte, Dept Mat Engn, Av Senador Salgado Filho 3000, BR-59078970 Natal, RN, Brazil

[2] Fed Univ Sao Del Rei, Dept Mech Engn, BR-36307352 Sao Joao Del Rei, MG, Brazil

[3] Univ Fed Rio Grande do Sul, Engn Sch, Dept Mat Engn, POB 15010, BR-91501970 Porto Alegre, RS, Brazil

[4] Texas A&M Univ, Dept Aerosp Engn, College Stn, TX 77843 USA

来源：

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING | 2019年 / 127卷

关键词：

Carbon/epoxy composites; Aging; Property degradation; Fatigue; Delamination; AEROSPACE COMPOSITE-MATERIALS; INTERFACE RELATED DAMAGE; PART II; EPOXY; EVOLUTION; MATRIX; GLASS;

D O I：

10.1016/j.compositesa.2019.105628

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This study concerns the effects of hygrothermal aging on failure of carbon/epoxy composites subjected to fatigue loading. AS4/8552 laminates with stacking sequence [0(2)/90(2)](s) are exposed to cycles of 4 hat 160 degrees C followed by 8 h of 80% average relative humidity at 70 degrees C, for a total exposure time of 2880 h. Fourier transform infrared (FTIR) spectroscopy, dynamic mechanical analysis (DMA), scanning electron microscopy (SEM) and change in weight, before and after hygrothermal exposure, are used to characterize the composites. Samples of plain epoxy 8552 are also exposed to the same aging conditions and characterized by optical microscopy (OM), FTIR spectroscopy and weight change. Stress-controlled tension-tension fatigue tests are then conducted using a stress ratio R = 0.1 and frequency of 5 Hz. The effects of hygrothermal aging on fatigue are interpreted by fatigue life diagrams as well as by studying evolution of ply crack density and delamination.

引用

页数：9

共 50 条

[41] Ply Scale Modeling and Fatigue Behavior of Glass/Carbon Epoxy Hybrid Composites
C. Hemanth Kumar
Arunkumar Bongale
Journal of Failure Analysis and Prevention, 2024, 24 (6) : 2912 - 2923
[42] EFFECTS OF INTERLEAVING ON THE IMPACT AND IMPACT FATIGUE RESPONSES OF CROSS-PLY CARBON-FIBER EPOXY LAMINATES
YUAN, Q
KARGERKOCSIS, J
POLYMERS & POLYMER COMPOSITES, 1995, 3 (03): : 171 - 179
[43] Multifractality of transverse cracking and cracks' length distribution in a cross-ply laminate under fatigue
Silberschmidt, VV
HenaffGardin, C
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1609 - 1614
[44] Local viscoelastic properties of a thermoplastic/carbon laminate as an indicator of fatigue damage
Minster, J. (minster@itam.cas.cz), 1600, Trans Tech Publications Ltd (606):
[45] A multiaxial fatigue failure criterion based on the principal constant life diagrams for unidirectional carbon/epoxy laminates
Kawai, M.
Teranuma, T.
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2012, 43 (08) : 1252 - 1266
[46] Statistical fatigue life prediction of cross-ply composite laminates
Diao, XX
Ye, L
Mai, YW
JOURNAL OF COMPOSITE MATERIALS, 1997, 31 (14) : 1442 - 1460
[47] Probabilistic analysis for the fatigue life of carbon/epoxy laminates
Kang, Ki-Weon
Lim, Dong-Min
Kim, Jung-Kyu
COMPOSITE STRUCTURES, 2008, 85 (03) : 258 - 264
[48] SIMULATION OF 90-DEGREES PLY FATIGUE-CRACK GROWTH ALONG THE WIDTH OF CROSS-PLY CARBON-EPOXY COUPONS
HENAFFGARDIN, C
URWALD, E
LAFARIEFRENOT, MC
MATERIALS SCIENCE, 1994, 30 (01) : 110 - 114
[49] Unfolding the early fatigue damage process for CFRP cross-ply laminates
Li, Xi
Kupski, Julian
De Freitas, Sofia Teixeira
Benedictus, Rinze
Zarouchas, Dimitrios
INTERNATIONAL JOURNAL OF FATIGUE, 2020, 140
[50] The Effect of Hygrothermal Aging on Mode I Fatigue Delamination Growth in a Carbon/Epoxy Composites
LaPlante, Gabriel
Landry, Benoit
JOURNAL OF ADVANCED MATERIALS, 2011, 43 (02): : 79 - 86

← 1 2 3 4 5 →