Thermodynamic properties and dissociation of SrLaGaO4

被引：1
|
作者：
Novoselov, AV
Ogorodova, LP
Zimina, GV
Pajaczkowska, A
机构：
[1] Lomonosov State Acad Fine Chem Technol, Moscow 117571, Russia
[2] Moscow State Univ, Moscow 119899, Russia
[3] Inst Elect Mat Technol, PL-01919 Warsaw, Poland
来源：
INORGANIC MATERIALS | 2000年 / 36卷 / 09期
关键词：
D O I：
10.1007/BF02758706
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The solution enthalpy of SrLaGaO4 in the 2PbO.B2O3 melt at 973 K was measured using a high-temperature Calvet microcalorimeter. The enthalpies of formation of SrLaGaO4 from the constituent oxides and constituent elements were determined to be -96.8 +/- 5.9 and -2128.7 +/- 6.1 kT/mol, respectively. The partial pressures of the vapor species over molten SrLaGaO4 at T-m = 1793 K were evaluated. The equilibrium oxygen pressure at 1793 K was found to be 4.13 x 10(-2) Pa.
引用
收藏
页码：929 / 931
页数：3
相关论文
共 50 条
  • [41] Thermodynamic properties and dissociation of SrLaAlO4
    A. V. Novoselov
    L. P. Ogorodova
    G. V. Zimina
    A. Pajaczkowska
    Inorganic Materials, 2000, 36 : 180 - 182
  • [42] Long persistent luminescence property of a novel green emitting SrLaGaO4: Tb3+ phosphor
    Fu, Xiaoyan
    Zheng, Shenghui
    Shi, Junpeng
    Li, Yuechan
    Zhang, Hongwu
    JOURNAL OF LUMINESCENCE, 2017, 184 : 199 - 204
  • [43] TEMPERATURE STUDY OF LATTICE-CONSTANTS AND RAMAN-SCATTERING OF SRLAGAO4 SINGLE-CRYSTAL
    DROZDOWSKI, M
    DOMAGALA, J
    KOZIELSKI, M
    SZYBOWICZ, M
    PAJACZKOWSKA, A
    SOLID STATE COMMUNICATIONS, 1995, 96 (10) : 785 - 788
  • [44] Contrast in transmission X-ray diffraction topographs of growth defects in the core of SrLaGaO4 single crystals
    Institute of Electronic Materials Technology, Wólczyn´ska 133, Warsaw, 01-919, Poland
    不详
    不详
    不详
    Malinowska, A. (agnieszka.malinowska@itme.edu.pl), 1600, International Union of Crystallography, 5 Abbey Road, Chester, CH1 2HU, United Kingdom (46):
  • [45] A Dy-based single ion magnet in a SrLaGaO4 matrix: enhanced parameters in an expanded crystal lattice
    Vasiliev, Alexander V.
    Sharifullin, Timur Z.
    Demidova, Elena D.
    Kremer, Reinhard K.
    Kazin, Pavel E.
    DALTON TRANSACTIONS, 2023, 52 (47) : 17747 - 17751
  • [46] Contrast in transmission X-ray diffraction topographs of growth defects in the core of SrLaGaO4 single crystals
    Malinowska, Agnieszka
    Lefeld-Sosnowska, Maria
    Haertwig, Juergen
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2013, 46 : 48 - 54
  • [47] Theoretical investigations on the electron paramagnetic resonance for Cr3+ in SrLaGaO4 and Cs2CdCl4 crystals
    Zeng, Ti-Xian
    Chen, Jia-Jun
    Chen, Tai-Hong
    Rengong Jingti Xuebao/Journal of Synthetic Crystals, 2010, 39 (SUPPL.): : 249 - 253
  • [48] Investigation of Eu3+ sites in SrLaGa3O7, SrLaGaO4 and SrLaAlO4 crystals
    RybaRomanowski, W
    Golab, S
    Pisarski, WA
    DominiakDzik, G
    Berkowski, M
    Pajaczkowska, A
    JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1997, 58 (04) : 639 - 645
  • [49] SrLaGaO4∶Dy3+荧光粉的制备及发光性能研究
    张恒
    陈伟
    姜锋
    朱德生
    稀土, 2023, 44 (06) : 28 - 37
  • [50] Optical Transitions and Excited State Absorption Cross Sections of SrLaGaO4 Doped with Ho3+ Ions
    Kaczkan, Marcin
    Malinowski, Michal
    MATERIALS, 2021, 14 (14)
12345