Application of the FRI crack growth model for neutron-irradiated stainless steels in high-temperature water of a boiling water reactor environment

被引：12

作者：

Koshiishi, Masato ^{[1
]}

Hashimoto, Tsuneyuki ^{[1
]}

Obata, Ryoji ^{[2
]}

机构：

[1] Nippon Nucl Fuel Dev, 2163 Narita Cho, Oarai, Ibaraki 3111313, Japan

[2] Hitachi GE Nucl Energy, 1-1,Saiwai Cho 3 Chome, Hitachi, Ibaraki 3170073, Japan

来源：

CORROSION SCIENCE | 2017年 / 123卷

关键词：

Austenitic stainless steel; BWR; Neutron irradiation; Irradiation assisted stress corrosion cracking; Crack growth rate; Modelling; QUANTITATIVE PREDICTION; CORROSION BEHAVIOR;

D O I：

10.1016/j.corsci.2017.04.025

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This study considered a methodology to reflect the effect on material properties by neutron irradiation onto the FRI model of the crack growth rate (CGR) of stress corrosion cracking developed at Tohoku University. Yield strength and strain hardening exponent were evaluated by a tensile test for irradiated stainless steels, and the relationship between mechanical property and strain to fracture of the oxide film was derived. Effect of the radiation-induced segregation on CGR was also discussed. The experimental tendencies for the CGR to increase with dose and almost saturate above 3 dpa were well replicated by the model calculations.

引用

页码：278 / 288

页数：11

共 50 条

[21] Prediction of crack growth resistance for ductile fracture of neutron-irradiated reactor pressure-vessel steels. Part 1
Margolin, B.Z.
Kostylev, V.I.
Problemy Prochnosti, 2001, (04): : 25 - 34
[22] Research of SCC Prediction Model for 304 Stainless Steel in the High-Temperature Water Environment
Y. H. Cui
J. L. Zhang
Strength of Materials, 2021, 53 : 573 - 581
[23] Prediction of crack growth resistance for ductile fracture for neutron-irradiated reactor pressure-vessel steels. Part 2
Margolin, B.Z.
Kostylev, V.I.
Problemy Prochnosti, 2001, (05): : 5 - 18
[24] Research of SCC Prediction Model for 304 Stainless Steel in the High-Temperature Water Environment
Cui, Y. H.
Zhang, J. L.
STRENGTH OF MATERIALS, 2021, 53 (04) : 573 - 581
[25] FATIGUE CRACK GROWTH OF STAINLESS STEEL PIPING IN A PRESSURIZED WATER REACTOR ENVIRONMENT.
Bamford, W.H.
1600,
[26] Factors affecting the crack growth rates of reactor pressure vessel steels under simulated boiling water reactor conditions
Chen, Y. Y.
Shih, H. C.
Wang, L. H.
Oung, J. C.
CORROSION, 2006, 62 (05) : 403 - 418
[27] SEARCH FOR ENHANCEMENT OF NEUTRON EMISSION FROM NEUTRON-IRRADIATED, DEUTERIDED, HIGH-TEMPERATURE SUPERCONDUCTORS IN A VERY LOW BACKGROUND ENVIRONMENT
CELANI, F
SPALLONE, A
LIBERATORI, L
CROCE, F
STORELLI, L
FORTUNATI, S
TULUI, M
SPARVIERI, N
FUSION TECHNOLOGY, 1992, 22 (01): : 181 - 186
[28] Stress corrosion cracking of stainless steels and nickel alloys in high-temperature water
Andresen, P. L.
Morra, M. M.
CORROSION, 2008, 64 (01) : 15 - 29
[29] CORROSION-RESISTANCE OF FERRITIC STAINLESS-STEELS IN HIGH-TEMPERATURE WATER
NAGANO, H
MIURA, M
TSUGE, H
KOSO, M
MARUYAMA, N
MINAMI, T
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (06) : B227 - B227
[30] EFFECT OF SURFACE TREATMENT ON CORROSION OF STAINLESS STEELS IN HIGH-TEMPERATURE WATER AND STEAM
WARZEE, M
HENNAUT, J
MAURICE, M
SONNEN, C
WATY, J
BERGE, P
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1965, 112 (07) : 670 - &

← 1 2 3 4 5 →