Effect of sulphide pollutants on mild steel corrosion in 3.5% NaCl solutions

被引：5
|
作者：
Wang, X. T. [1 ]
Hou, B. R. [1 ]
机构：
[1] Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China
来源：
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY | 2010年 / 45卷 / 01期
关键词：
Sulphide pollutants; Mild steel; Corrosion; Pitting; COPPER-NICKEL-ALLOYS; ELECTROCHEMICAL-BEHAVIOR; EROSION-CORROSION; CARBON-STEEL; SEAWATER;
D O I：
10.1179/147842209X12476568584188
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Corrosion behaviour of mild steel in 3.5% NaCl solution containing sulphide pollutants was investigated using potentiodynamic polarisation measurement, electrochemical impedance spectroscopy and scanning electron microscopy. Reaction and mechanism of the corrosion process were discussed. The study shows that sulphide concentration had a remarkable effect on pitting corrosion. Sulphide pollutants exhibited inhibition effect with passive film in the initial stage of corrosion. When the passive film breaks down, sulphide would accelerate the corrosion process.
引用
收藏
页码：57 / 60
页数：4
相关论文
共 50 条
  • [41] Fabrication and characterization of bimetallic nickel-molybdenum nanocoatings for mild steel corrosion protection in 3.5% NaCl solution
    Meymian, Mohammad Reza Zamani
    Ghaffarinejad, Ali
    Fazli, Reza
    Mehr, Ali Kosari
    COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2020, 593
  • [42] Coatings Corrosion Resistance of Poly(o-Phenylenediamine) on Mild Steel in 3.5% NaCl: Influence of Inorganic Acid
    Zhang, Jia-Wei
    Li, Ying
    Ding, Yu-Shi
    Pan, Ke-Feng
    Zhao, Qing
    JOM, 2020, 72 (12) : 4288 - 4295
  • [43] The effect of stoving temperature on the corrosion inhibition of a polymeric film on mild steel in NaCl
    Bertolotto, C
    Beccaria, AM
    CORROSION PREVENTION & CONTROL, 1996, 43 (01): : 7 - 13
  • [44] Calicotome Extract as a Friendly Corrosion Inhibitor of Carbon Steel in Polluted NaCl (3.5% NaCl
    Fouda, A. S.
    Killa, H. M.
    Farouk, A.
    Salem, A. M.
    EGYPTIAN JOURNAL OF CHEMISTRY, 2019, 62 (10): : 1879 - 1894
  • [45] Effect of temperature on corrosion behavior of X70 pipeline steel in 3.5% NaCl solution
    Wu, Meijun
    Gao, Zhiming
    Wu, Shixiong
    Liu, Yingjie
    Hu, Wenbin
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (06): : 1 - 14
  • [46] Evaluation of corrosion and erosion-corrosion resistances of mild steel in sulfide-containing NaCl aerated solutions
    Hamdy, Abdel Salam
    Sa'eh, A. G.
    Shoeib, M. A.
    Barakat, Y.
    ELECTROCHIMICA ACTA, 2007, 52 (24) : 7068 - 7074
  • [47] The effect of applied stress on the crevice corrosion of 304 stainless steel in 3.5 wt% NaCl solution
    Zhu, L. Y.
    Cui, Z. Y.
    Cui, H. Z.
    Wang, X.
    Li, Y. Z.
    CORROSION SCIENCE, 2022, 196
  • [48] Inhibition of steel corrosion in NaCl solutions by samarium
    Ortega, R
    Beltran, D
    Meas, Y
    Becerril, A
    JOURNAL OF THE BRAZILIAN CHEMICAL SOCIETY, 1997, 8 (02) : 149 - 152
  • [49] Metastable pitting corrosion of 304 stainless steel in 3.5% NaCl solution
    Tian, Wenming
    Du, Nan
    Li, Songmei
    Chen, Sibing
    Wu, Qunying
    CORROSION SCIENCE, 2014, 85 : 372 - 379
  • [50] Effects of Cinnamaldehyde as an Eco-Friendly Corrosion Inhibitor on Mild Steel in Aerated NaCl Solutions
    S. M. Zakir Hossain
    S. A. Kareem
    A. F. Alshater
    H. Alzubair
    S. A. Razzak
    M. M. Hossain
    Arabian Journal for Science and Engineering, 2020, 45 : 229 - 239
12345