Pore size effects on Ru/SiO2 catalysts with Mn and Zr promoters for Fischer-Tropsch synthesis

被引：22

作者：

Nurunnabi, Mohammad ^{[1
]}

Turn, Scott Q. ^{[1
]}

机构：

[1] Univ Hawaii Manoa, Hawaii Nat Energy Inst, Honolulu, HI 96822 USA

来源：

FUEL PROCESSING TECHNOLOGY | 2015年 / 130卷

关键词：

Pore size; Ru/SiO2; catalyst; Mn and Zr addition; Fischer-Tropsch synthesis; Catalyst activity; Deactivation rate; MGO SOLID-SOLUTION; PRESSURIZED CONDITIONS; COBALT CATALYSTS; NOBLE-METALS; PERFORMANCE; METHANE; SELECTIVITY; RESISTANCE; RU/AL2O3;

D O I：

10.1016/j.fuproc.2014.10.004

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

The effects of pore size on Ru/SiO2 catalyst performance were investigated for Fischer-Tropsch synthesis under the conditions of 503 K, 20 bar and 1800 h(-1). Ru/SiO2 with 10 nm pore size catalyst showed higher catalytic activity than Ru/SiO2 catalysts with 3, 6 and 30 nm pore sizes. The 10 nm pore size, Ru/SiO2 catalyst exhibited uniform pore diameter, an increased surface concentration of active Ru metals, and the increased dispersion of Ru on the surface compared to the other pore diameters. Deactivation was clearly observed for all Ru/SiO2 catalysts during the reaction. The addition of small amounts of Zr and Mn (1:30, Zr or Mn:Si) improved catalytic activity and stability for Fischer-Tropsch synthesis. The deactivation rate of Ru/Zr/Q10 was about 21% at 51 h time on stream and this rate was much lower than Ru/Q10 (57%). Ru/Mn/Q10 showed higher catalytic activity than Ru/Q10 and Ru/Zr/Q10, and its deactivation rate was much lower -9% after 51 h time on stream. The small amount of Mn added to the Ru/SiO2 increased the concentration of active Ru metals and enhanced their dispersion on the support surface. (C) 2014 Elsevier B.V. All rights reserved.

引用

下载

页码：155 / 164

页数：10

共 50 条

[31] Study on bimodal mesoporous Co/SiO2 catalysts for the Fischer-Tropsch synthesis
Guo, Cuili
Wu, Yuanyuan
Zhan, Jishan
REACTION KINETICS MECHANISMS AND CATALYSIS, 2013, 109 (02) : 497 - 508
[32] Influence of pore regularity on Fischer–Tropsch synthesis with Co/SiO2 Catalysts
Yuelun Wang
Bo Hou
Jiangang Chen
Yuhan Sun
Reaction Kinetics, Mechanisms and Catalysis, 2011, 102 : 155 - 164
[33] CO/SiO2 sol-gel catalysts for Fischer-Tropsch synthesis
Bianchi, CL
Martini, F
Moggi, P
CATALYSIS LETTERS, 2001, 76 (1-2) : 65 - 69
[34] Fischer-Tropsch synthesis over Co/SiO2 catalysts modified with ethylenediamine
Wang, Yuelun
Hou, Bo
Li, Debao
Chen, Jiangang
Sun, Yuhan
RENEWABLE AND SUSTAINABLE ENERGY II, PTS 1-4, 2012, 512-515 : 2143 - +
[35] Characterization of Ru/Q10 catalysts containing Zr or Mn and their activity for Fischer-Tropsch synthesis
Nurunnabi, Mohammad
Turn, Scott Q.
FUEL PROCESSING TECHNOLOGY, 2015, 138 : 490 - 499
[36] Effects of Ru precursors on activity of Ru-SiO2 catalysts prepared by alkoxide method in Fischer-Tropsch synthesis
Okabe, Kiyomi
Takahara, Isao
Inaba, Megumu
Murata, Kazuhisa
Yoshimura, Yuji
JOURNAL OF THE JAPAN PETROLEUM INSTITUTE, 2007, 50 (01) : 65 - 68
[37] Fischer-Tropsch synthesis in slurry-phase reactors over Mn- and Zr-modified Co/SiO2 catalysts
Liu, Yanyong
Hanaoka, Toshiaki
Miyazawa, Tomohisa
Murata, Kazuhisa
Okabe, Kiyomi
Sakanishi, Kinya
FUEL PROCESSING TECHNOLOGY, 2009, 90 (7-8) : 901 - 908
[38] Promotion of CO/SiO2 Fischer-Tropsch catalysts with zirconium
Moradi, GR
Basir, MM
Taeb, A
Kiennemann, A
CATALYSIS COMMUNICATIONS, 2003, 4 (01) : 27 - 32
[39] Pore size effect of mesoporous support on metal particle size of Co/SiO2 catalyst in Fischer-Tropsch synthesis
Intarasiri, Saowaluk
Ratana, Tanakorn
Sornchamni, Thana
Tungkamani, Sabaithip
Phongaksorn, Monrudee
INTERNATIONAL JOURNAL OF ADVANCED AND APPLIED SCIENCES, 2018, 5 (11): : 80 - 85
[40] TiO2 promoted Co/SiO2 catalysts for Fischer-Tropsch synthesis
Hinchiranan, Sukamon
Zhang, Yi
Nagamori, Satoshi
Vitidsant, Tharapong
Tsubaki, Noritatsu
FUEL PROCESSING TECHNOLOGY, 2008, 89 (04) : 455 - 459

← 1 2 3 4 5 →