From size-dependent strengthening to softening in nanolaminated Cu/Cu-Zr crystalline/amorphous micropillars

被引：3
|
作者：
Wang, Y. Q. [1 ]
Liang, X. Q. [1 ]
Wu, K. [1 ]
Zhang, J. Y. [1 ]
Liu, G. [1 ]
Sun, J. [1 ]
机构：
[1] Xi An Jiao Tong Univ, State Key Lab Mech Behav Mat, Xian 710049, Shaanxi, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2018年 / 732卷
基金：
中国国家自然科学基金; 中国博士后科学基金;
关键词：
Crystalline/amorphous nanolaminates; Micropillars; Flow stress; Size effect; Deformation behavior; SHEAR BANDS; DEFORMATION; PLASTICITY; MECHANISMS; TRANSITION; BEHAVIOR;
D O I：
10.1016/j.msea.2018.06.079
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Microcompressive tests were performed to investigate the intrinsic modulation effect and extrinsic diameter effect on strength and deformation behaviors of nanolaminated Cu/Cu-Zr crystalline/amorphous micropillars within a diameter D range from 300 to 1500 nm as well as a modulation ratio eta range from 0.1 to 3.0. Experimental results revealed a transition of D-dependent deformation mode from homogeneous-like to shear localization at large eta, while D-independent homogeneous extrusion of Cu at small eta. Furthermore, the flow strength increased with raising D at small eta, but decreased at large eta, exhibiting a D-insensitive strength at a critical eta* similar to 0.5. These unusual results were rationalized in terms of a coupling effect of dislocation actions and shear transformation zone mediated operations.
引用
收藏
页码：29 / 34
页数：6
相关论文
共 50 条
  • [31] Electrochemical modification of Cu-Zr amorphous alloys for catalysts
    Janik-Czachor, M
    Szummer, A
    Molnar, A
    Dolata, M
    Kudelski, A
    Varga, M
    Bukowska, J
    Sikorski, K
    ELECTROCHIMICA ACTA, 2000, 45 (20) : 3295 - 3303
  • [32] THE CHANGE OF THERMOPOWER ON CRYSTALLIZATION OF AMORPHOUS CU-ZR ALLOYS
    SHEARWOOD, C
    GREIG, D
    SOLID STATE COMMUNICATIONS, 1989, 71 (03) : 207 - 209
  • [33] MECHANICAL-PROPERTIES OF AMORPHOUS CU-ZR ALLOY
    TOMIZAWA, S
    MASUMOTO, T
    SCIENCE REPORTS OF THE RESEARCH INSTITUTES TOHOKU UNIVERSITY SERIES A-PHYSICS CHEMISTRY AND METALLURGY, 1977, 26 (4-5): : 263 - 269
  • [34] MECHANICAL-PROPERTIES OF AN AMORPHOUS CU-ZR ALLOY
    VITEK, JM
    GRANT, NJ
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (07): : 1472 - 1473
  • [35] Thermal and mechanical behaviors of Cu-Zr amorphous alloys
    Kwon, Oh-Jib
    Lee, Young-Kook
    Park, Sang-Ok
    Lee, Jae-Chul
    Kim, Yu-Chan
    Fleury, Eric
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 449 : 169 - 171
  • [36] CU PRECIPITATIONS AT THE SURFACE OF CRYSTALLINE CU-ZR ALLOYS AFTER ANNEALING IN HYDROGEN
    YU, XN
    SCHLAPBACH, L
    ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE NEUE FOLGE, 1989, 164 : 1171 - 1176
  • [37] Size effect on atomic structure in low-dimensional Cu-Zr amorphous systems
    Zhang, W. B.
    Liu, J.
    Lu, S. H.
    Zhang, H.
    Wang, H.
    Wang, X. D.
    Cao, Q. P.
    Zhang, D. X.
    Jiang, J. Z.
    SCIENTIFIC REPORTS, 2017, 7
  • [38] Size effect on atomic structure in low-dimensional Cu-Zr amorphous systems
    W. B. Zhang
    J. Liu
    S. H. Lu
    H. Zhang
    H. Wang
    X. D. Wang
    Q. P. Cao
    D. X. Zhang
    J. Z. Jiang
    Scientific Reports, 7
  • [39] Unique irradiation damage behavior and deformation mechanisms in crystalline/amorphous Ag/Cu-Zr nanolaminates
    Li, Z. A.
    Zuo, J. D.
    Wang, Y. Q.
    Wu, K.
    Zhang, J. Y.
    Liu, G.
    Sun, J.
    ACTA MATERIALIA, 2024, 276
  • [40] Wet oxidation of amorphous and crystalline Cu-Zr alloys probed by thermodynamic, kinetic, and instrumental analyses
    Ma, Shuo
    Liu, Panmei
    Liu, Yongchang
    Wang, Zumin
    CORROSION SCIENCE, 2025, 242
12345