Composition, temperature, and crystal orientation dependence of the linear electro-optic properties of Pb(Zn1/3Nb2/3)O3-PbTiO3 single crystals

被引：59
|
作者：
Barad, Y [1 ]
Lu, Y [1 ]
Cheng, ZY [1 ]
Park, SE [1 ]
Zhang, QM [1 ]
机构：
[1] Penn State Univ, Mat Res Lab, University Pk, PA 16802 USA
来源：
APPLIED PHYSICS LETTERS | 2000年 / 77卷 / 09期
关键词：
D O I：
10.1063/1.1290156
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The linear electro-optic (EO) coefficients of Pb(Zn1/3Nb2/3)O-3-PbTiO3 single crystals over a broad composition range were investigated at temperatures from -20 to 80 degrees C. The orientation effect on the EO coefficients was also examined. For crystals poled in the < 001 > direction, a large r(33) was observed near the morphotropic phase boundary (MPB). More importantly, r(33) was found to be independent of temperature for the crystals on the tetragonal side of the MPB. In contrast, r(13) was nearly zero for all compositions examined at all the temperatures. The large r(33) near the MPB and the observed crystal orientation effect of the EO coefficients were also analyzed. (C) 2000 American Institute of Physics. [S0003-6951(00)02735-2].
引用
收藏
页码：1247 / 1249
页数：3
相关论文
共 50 条
  • [31] Ferroelastic switching and elastic nonlinearity in ⟨001⟩-oriented Pb(Mg1/3Nb2/3)O3-PbTiO3 and Pb(Zn1/3Nb2/3)O3-PbTiO3 crystals
    Viehland, D
    Powers, J
    Ewart, L
    Li, JF
    JOURNAL OF APPLIED PHYSICS, 2000, 88 (08) : 4907 - 4909
  • [32] Polarized Raman Study in Pb(Zn1/3Nb2/3)O3-PbTiO3 Mixed Crystal
    Iwata, Makoto
    Hasegawa, Yusuke
    Aoyagi, Rintaro
    Maeda, Masaki
    Wakiya, Naoki
    Suzuki, Hisao
    Ishibashi, Yoshihiro
    FERROELECTRICS, 2008, 376 : 270 - 276
  • [33] Switching current measurements in Pb(Zn1/3Nb2/3)O3-PbTiO3 relaxor ferroelectric single crystals
    Belegundu, U
    Uchino, K
    JOURNAL OF ELECTROCERAMICS, 2001, 6 (02) : 109 - 114
  • [34] Growth and characterization of Fe-doped Pb(Zn1/3Nb2/3)O3-PbTiO3 single crystals
    Zhang, SJ
    Lebrun, L
    Jeong, DY
    Randall, CA
    Zhang, QM
    Shrout, TR
    JOURNAL OF APPLIED PHYSICS, 2003, 93 (11) : 9257 - 9262
  • [35] Microhardness and fracture toughness of ⟨111⟩-oriented Pb(Zn1/3Nb2/3)O3-PbTiO3 single crystal
    Jin, Min
    Xu, Jiayue
    Li, Xinhua
    Shen, Hui
    He, Qingbo
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 472 (1-2): : 353 - 357
  • [36] Domain switching and electromechanical properties of pulse poled Pb(Zn1/3Nb2/3)O3-PbTiO3 crystals
    Yu, HX
    Gopalan, V
    Sindel, J
    Randall, CA
    JOURNAL OF APPLIED PHYSICS, 2001, 89 (01) : 561 - 567
  • [37] Phased array ultrasonic probe using Pb(Zn1/3Nb2/3)O3-PbTiO3 single crystal
    Saitoh, S
    Kobayashi, T
    Harada, K
    Shimanuki, S
    Yamashita, Y
    ULTRASONIC TRANSDUCER ENGINEERING: MEDICAL IMAGING 1998, 1998, 3341 : 264 - 271
  • [38] Elastic modulus, hardness and fracture behavior of Pb(Zn1/3Nb2/3)O3-PbTiO3 single crystal
    Zeng, Kaiyang
    Pang, Yong-Song
    Shen, Lu
    Rajan, K. K.
    Lim, Leong-Chew
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 472 (1-2): : 35 - 42
  • [39] Giant electromechanical coupling factor of K31 mode in Pb(Zn1/3Nb2/3)O3-PbTiO3 and Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals
    Ogawa, T.
    Matsushita, M.
    Yoshioka, K.
    FERROELECTRICS, 2006, 339 : 1689 - 1697
  • [40] Orientation dependence properties of modified tetragonal 0.88Pb(Zn1/3Nb2/3)O3-0.12PbTiO3 single crystals
    Zhang, SJ
    Lebrun, L
    Randall, CA
    Shrout, TR
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2005, 202 (01): : 151 - 157
12345