Analysis of crack formation of Y123 single crystal substrate fabricated by the pulling method

被引：0
|
作者：
Egami, M [1 ]
Itoga, N [1 ]
Koyama, S [1 ]
Izumi, T [1 ]
Shiohara, Y [1 ]
机构：
[1] ISTEC, Superconduct Res Lab, Koto Ku, Tokyo 1350062, Japan
来源：
ADVANCES IN SUPERCONDUCTIVITY XII | 2000年
关键词：
crack formation; chemical etching; single crystal substrate;
D O I：
暂无
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
We prepared a substrates by slicing an as-grown YBa2Cu3O7-x single crystal and a typical heating cycle was applied in the Air (750 degrees C /hour as increase/decrease rate up to 750 degrees C) which is similar to the film vapor deposition process to the wafer, and an additional crack formation was observed. We also found that in the case of the Ar atmosphere (1.5%O-2), no additional crack was formed even at the same heating cycle. This indicated that the origin of the additional crack formation was not only the effect of the thermal distortion but also that of the lattice distortion due to the oxygen diffusion or the mixture effect.
引用
收藏
页码：945 / 947
页数：3
相关论文
共 50 条
  • [1] Growth process of Y123 crystal grains in the film fabricated by TFA-MOD method
    Mori, N.
    Yoshida, K.
    Miyanaga, Y.
    Yamada, K.
    Teranishi, R.
    Mukaida, M.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (15-20): : 1341 - 1344
  • [2] Crystal growth process of Y123 film fabricated by modified TFA-MOD process
    Mori, N.
    Mukaida, M.
    Teranishi, R.
    Yamada, K.
    Tanaka, T.
    Tada, K.
    8TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS'07), 2008, 97
  • [3] Microstructure formation process of Y123 film fabricated by advanced TFA-MOD process
    Mori, Nobuyuki
    Tanaka, Takayuki
    Minei, Taichi
    Yamada, Kazuhiro
    Mukaida, Masasi
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2007, 17 (02) : 3290 - 3293
  • [4] Influence of thickness on alignments of Y123 films fabricated on metallic substrates using PLD method
    Kakimoto, K
    Iijima, Y
    Takeda, K
    PHYSICA C, 2001, 357 : 975 - 978
  • [5] Phase-field analyses for Y123 crystal growth
    Egami, A
    Nakamura, Y
    Izumi, T
    Shiohara, Y
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2001, 357 : 1411 - 1415
  • [6] Recrystallization texture and microstructure of metal substrate for Y123 coated superconductor
    Liu, HZ
    Shi, K
    Yang, J
    Yuan, GS
    JOURNAL OF RARE EARTHS, 2003, 21 (04) : 450 - 452
  • [7] Phase relation in Y211-Y123-Ag system and morphology of silver in Y123 crystal
    Nakamura, Y
    Tachibana, K
    Kato, S
    Ban, T
    Yoo, SI
    Fujimoto, H
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1998, 294 (3-4): : 302 - 315
  • [8] Effect of pulling rate on transport property of directionally solidified Y123 superconducting fiber
    Misu, T
    Oolshl, Y
    Inada, R
    Nakamura, Y
    Oota, A
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 1021 - 1025
  • [9] Recrystallization Texture and Microstructure of Metal Substrate for Y123 Coated Superconductor
    刘慧舟
    史锴
    杨坚
    袁冠森
    JournalofRareEarths, 2003, (04) : 450 - 452
  • [10] Three-dimensional observation of microstructures in Y123 films fabricated by TFA-MOD method
    Yamada, K.
    Mitsuhara, M.
    Hata, S.
    Miyanaga, Y.
    Teranishi, R.
    Mori, N.
    Mukaida, M.
    Kaneko, K.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (15-20): : 1446 - 1449
12345