High-temperature internal oxidation behavior of surface cracks in low alloy steel bloom

被引：21
|
作者：
Xing, Lidong [1 ]
Gu, Chao [1 ]
Lv, Ziyu [1 ]
Bao, Yanping [1 ]
机构：
[1] Univ Sci & Technol Beijing USTB, Tech Support Ctr Prevent & Control Disastrous Acc, State Key Lab Adv Met, Beijing 100083, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 197卷
基金：
中国博士后科学基金;
关键词：
Low alloy steel; Raman spectroscopy; High-temperature oxidation; Internal oxidation; Interfaces; CONTINUOUS-CASTING BLOOM; AUSTENITIC STAINLESS-STEEL; PWR PRIMARY WATER; HEAVY REDUCTION; RAMAN-SPECTROSCOPY; IRON-OXIDES; SCALE; KINETICS; MICROSTRUCTURE; MECHANISMS;
D O I：
10.1016/j.corsci.2021.110076
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The oxidation behavior and mechanism near the crack of bloom was investigated by prefabricated crack and oxidation at high temperature (1000 - 1200 degrees C). The interface oxide layer composed of Fe2SiO4 and FeCr2O4 can prevent the steel matrix from being oxidized. However, the melting point of Fe2SiO4 is approximately 1170 degrees C, so the interface oxide layer is in a metastable state with the progress of high-temperature oxidation. At this time, the thickness of the internal oxidation spot layer in the steel matrix increases rapidly. As a result, internal oxidation mechanism of surface cracks at high temperature is clarified.
引用
收藏
页数：12
相关论文
共 50 条
  • [31] High-Temperature Oxidation Behavior and Grinding Performance of CoCrFeMnNi High-Entropy Alloy
    Zhang, Jiangyu
    Liu, Yueqiu
    Chen, Yanling
    Liu, Shizhao
    ADVANCED ENGINEERING MATERIALS, 2025, 27 (04)
  • [32] Effect of Y on the high-temperature oxidation behavior of CrMoTaTi refractory high entropy alloy
    Du, Yuhang
    Ding, Deyu
    Lai, Limin
    Xiao, Siming
    Guo, Ning
    Song, Bo
    Guo, Shengfeng
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2022, 103
  • [33] High temperature oxidation behavior of low temperature aluminized Mirrax® ESR steel
    Yener, Tuba
    Doleker, Kadir Mert
    Erdogan, Azmi
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [34] HIGH-TEMPERATURE INTERNAL OXIDATION BEHAVIOR OF DILUTE NI-AL ALLOYS
    HINDAM, H
    WHITTLE, DP
    JOURNAL OF MATERIALS SCIENCE, 1983, 18 (05) : 1389 - 1404
  • [35] The oxidation behavior of high-temperature aluminides
    I. C. I. Okafor
    R. G. Reddy
    JOM, 1999, 51 : 35 - 40
  • [36] High-temperature oxidation behavior and surface roughness evolution of VPSNiCrAlY coating
    Seo, D.
    Ogawa, K.
    Shoji, T.
    Murata, S.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2008, 17 (01) : 136 - 143
  • [37] Study on surface oxidation behavior of pourous NiTi alloy at high temperature
    Li, Qiang
    Zhang, XiaoNa
    MATERIALS AND MANUFACTURING, PTS 1 AND 2, 2011, 299-300 : 534 - +
  • [38] High-temperature steam oxidation behavior of an FeCrAl alloy with controlled addition of Mo
    Qi, Wen
    Yang, Kun
    Wang, Peng
    Du, Shiyu
    Bai, Chengying
    Wang, Xiaodong
    Qiao, Yingjie
    Zheng, Ting
    Zhang, LiLi
    Zhang, Xiaohong
    JOURNAL OF MATERIALS SCIENCE, 2022, 57 (44) : 20909 - 20927
  • [39] Research on high-temperature oxidation resistance behavior of TNM titanium aluminum alloy
    Di, Shixiong
    Ou, Baiyu
    Li, Wei
    Zhao, Chunling
    Nie, Jianhao
    You, Ruyue
    Ji, Xiankun
    Zhao, Yu
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2024, 46 (10): : 1826 - 1833
  • [40] High-Temperature Oxidation Behavior of a Ni-Cr-W-Al Alloy
    Y.C. Ma
    Journal of Materials Science & Technology, 2011, 27 (09) : 841 - 845
12345