Fabrication and properties of W-Cu alloy reinforced by multi-walled carbon nanotubes

Multi-walled carbon nanotubes (MWCNTs) coated with copper by electroless plating and W-Cu powder fabricated by mechanical alloying were mixed by ball-milling in ethanol solution. MWCNTs/W-Cu composites with improved mechanical properties and thermal conductivity were fabricated by hot-pressing sintering process at temperature 1400 degrees C under a pressure of 30 MPa for 2 h in pure Ar atmosphere. Effects of doping amounts of Cu-coated MWCNTs on the density, microstructure, thermal conductivity and mechanical properties were investigated. The bending strength and thermal conductivity of the 0.4 wt.% MWCNTs/W-Cu composites, compared with the monolithic W-Cu alloy, were enhanced 8.8% and 27.8%, respectively. (c) 2006 Elsevier B.V. All rights reserved.