Influence of different sulfur compounds on corrosion due to naphthenic acid

被引：58
|
作者：
Yépez, O [1 ]
机构：
[1] Mem Univ Newfoundland, Dept Chem, St Johns, NF A1B 3X7, Canada
来源：
FUEL | 2005年 / 84卷 / 01期
关键词：
sulfur compounds; naphthenic acid corrosion; mechanism;
D O I：
10.1016/j.fuel.2004.08.003
中图分类号：
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号：
0807 ; 0820 ;
摘要：
The influence of different sulfur compounds on corrosion due to naphthenic acid was studied by means of the new method FeNCOR(TM). It was found that such influence occurs after the reduction of the given sulfur compound by the cathodic reaction of the overall process of naphthenic acid corrosion. When the reduction product is H2S the formation of a potentially protective layer of FeS occurs, whereas when the reduction product is H2O, coming from the reduction of sulfoxides, the naphthenic acid corrosion is enhanced. These findings help to understand crude oil corrosivity behavior and serve as a warning for blending. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：97 / 104
页数：8
相关论文
共 50 条
  • [41] Sulfur Containing Compounds as Corrosion Inhibitors for Mild Steel in Hydrochloric Acid Solution
    Jafari, Hojat
    Sayin, Koray
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (03) : 805 - 815
  • [42] Corrosion of stainless steels in acid solutions with organic sulfur-containing compounds
    Cheng, XL
    Ma, HY
    Chen, SH
    Yu, R
    Chen, X
    Yao, ZM
    CORROSION SCIENCE, 1999, 41 (02) : 321 - 333
  • [43] Sulfur Containing Compounds as Corrosion Inhibitors for Mild Steel in Hydrochloric Acid Solution
    Hojat Jafari
    Koray Sayin
    Transactions of the Indian Institute of Metals, 2016, 69 : 805 - 815
  • [44] CORROSION PROBLEMS OF SULFUR COMPOUNDS IN PETROLEUM
    HUDGINS, CM
    ERDOL UND KOHLE ERDGAS PETROCHEMIE, 1969, 22 (07): : 429 - &
  • [45] Influence of Aging in Different Oak Barrels on Volatile Sulfur Compounds in Wines
    不同类型橡木桶陈酿对葡萄酒中 挥发性硫化物的影响
    Duan, Changqing (chqduan@cau.edu.cn), 1600, Chinese Chamber of Commerce (41):
  • [46] Cure behavior of EPDM compounds - Influence of different accelerated sulfur systems
    Markovic, MG
    Choudhury, NR
    Dimopoulos, M
    Matisons, JG
    Williams, DRG
    KAUTSCHUK GUMMI KUNSTSTOFFE, 1999, 52 (03): : 170 - +
  • [47] Flow accelerated naphthenic acid corrosion during high acid crude oil refining
    Zhang Xiaofei
    Ma Tao
    Hua Xiaochun
    Zheng Jinde
    Wang Xiaoyi
    Rao Sixian
    ENGINEERING FAILURE ANALYSIS, 2020, 117
  • [48] Corrosion characteristics of electroless Ni-P coating in naphthenic acid
    Department of Environmental Engineering, Wuhan, China
    不详
    不详
    Mater Perform, 2009, 4 (38-42):
  • [49] Analysis of Oxide Scales Formed in the Naphthenic Acid Corrosion of Carbon Steel
    Jin, Peng
    Bota, Gheorghe
    Robbins, Winston
    Nesic, Srdjan
    ENERGY & FUELS, 2016, 30 (08) : 6853 - 6862
  • [50] Corrosion Characteristics of Electroless Ni-P Coating in Naphthenic Acid
    Chen, Zhiliang
    Lin, An
    Gan, Fuxing
    Fang, Dajing
    Hao, Long
    Zhang, Yeming
    MATERIALS PERFORMANCE, 2009, 48 (04) : 38 - 42
12345