A novel self-embrittling strippable coating for radioactive decontamination based on silicone modified styrene-acrylic emulsion

Silicone modified styrene-acrylic emulsion and butyl acrylate were used as a main film-forming agent and an additive respectively to synthesize a self-embrittling strippable coating. The doping mass-ratio of butyl acrylate was adjusted at 0, 5%, 10%, 15%, 20%, and the results indicated the optimized doping ratio was 10%. Ca(OH)(2) was used to promote the coating film self-embrittling at a moderate doping mass-ratio of 20%. The synthesized coating's coefficients of alpha and beta decontamination on concrete, marble, glass and stainless steel surfaces were both greater than 85%, which indicated the synthesized coating is a promising cleaner for radioactive decontamination.