A New Alloying Concept for Low-Density Steels

This paper introduces a new alloying concept for low-density steels. Based on model calculations, samples-or "heats"-with 0.7 wt% C, 1.45 wt% Si, 2 wt% Cr, 0.5 wt% Ni, and an aluminium content varying from 5 to 7 wt% are prepared. The alloys are designed to obtain steel with reduced density and increased corrosion resistance suitable for products subjected to high dynamic stress during operation. Their density is in the range from 7.2 g cm(-3) to 6.96 g cm(-3). Basic thermophysical measurements are carried out on all the heats to determine the critical points of each phase transformation in the solid state, supported by metallographic analysis on SEM and LM or the EDS analysis of each phase. It is observed that even at very high austenitisation temperatures of 1100 degrees C, it is not possible to change the two-phase structure of ferrite and austenite. A substantial part of the austenite is transformed into martensite during cooling at 50 degrees C s(-1). The carbide kappa phase is segregated at lower cooling rates (around 2.5 degrees C s(-1)).