A deep-sea corrosion study on titanium and Ti6A14V alloy

被引：0
|
作者：
Venkatesan, R [1 ]
Dwarakadasa, ES
Ravindran, M
机构：
[1] Natl Inst Ocean Technol, Madras, Tamil Nadu, India
[2] Indian Inst Sci, Dept Met, Bangalore 560012, Karnataka, India
来源：
CORROSION PREVENTION & CONTROL | 2004年 / 51卷 / 03期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
THE CORROSION behaviour of titanium and titanium alloy Ti-6Al-4V in a deep-sea environment the Indian Ocean is presented. For the first time, coupons of these materials were exposed for longer duration at great depth in the ocean. Weight-loss measurements did not show any corrosion of the titanium or the alloy at depths of 500, 1200, 3500, and 5100m. Tensile tests were carried out on the deep-sea exposed specimens, and were compared with unexposed control specimens. The results show that the tensile strength did not change after deep-sea exposure.
引用
收藏
页码：98 / 103
页数：6
相关论文
共 50 条
  • [21] Ultrasonic impact treatment induced oxidation of Ti6A14V alloy
    Vasylyev, M. A.
    Chenakin, S. P.
    Yatsenko, L. F.
    ACTA MATERIALIA, 2016, 103 : 761 - 774
  • [22] Corrosion properties of TiN prepared by laser gas alloying of Ti and Ti6A14V
    Deptartment of Corros. and Protect., Ctro. Nac. de Invest. Metalurgicas, Avenida de Gregorio del Amo, 8, E-28040 Madrid, Spain
    Corros. Sci., 8 (1411-1419):
  • [23] Wear properties of nonhydrogenated,hydrogenated,and dehydrogenated Ti6A14V alloy
    Bao-Guo Yuan
    Hai-Ping Yu
    Chun-Feng Li
    Dong-Li Sun
    Rare Metals, 2018, 37 (07) : 574 - 578
  • [24] Understanding the wire electrical discharge machining of Ti6A14V alloy
    Pramanik, A.
    Basak, A. K.
    Prakash, C.
    HELIYON, 2019, 5 (04)
  • [25] Corrosion-induced deceleration-to-acceleration of fatigue crack growth for deep-sea Ti6Al4V ELI titanium alloy
    Zhao, Yuxiang
    Yu, Peishi
    Wu, Liansheng
    Zhang, Xin
    Wei, Pengyu
    Zhao, Junhua
    ENGINEERING FRACTURE MECHANICS, 2023, 281
  • [26] Ti6A14V的激光涂层
    李华伦
    Molian P.A.
    航空学报, 1990, (08) : 405 - 409
  • [27] Preparation of Ti6A14V Alloy Powder by Multistage Depth Reduction Process
    Yan Jisen
    Dou Zhihe
    Zhang Tingan
    Niu Liping
    RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (08) : 2973 - 2978
  • [28] Plasma nitriding of Ti6A14V alloy for improved water erosion resistance
    Batory, D.
    Szymanski, W.
    Panjan, M.
    Zabeida, O.
    Klemberg-Sapieha, J. E.
    WEAR, 2017, 374 : 120 - 127
  • [29] ELECTROCHEMICAL FABRICATION OF BIOACTIVE COMPOSITE COATINGS ON TI6A14V SURGICAL ALLOY
    SHIRKHANZADEH, M
    MATERIALS LETTERS, 1992, 14 (01) : 27 - 30
  • [30] Fatigue limit of Ti6A14V alloy produced by Selective Laser Sintering
    Benedetti, M.
    Cazzolli, M.
    Fontanari, V.
    Leoni, M.
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 3158 - 3167
12345