Electrochemical study of the corrosion processes of the secondary side of steam generators

被引：0

作者：

Sala, B ^{[1
]}

Chevalier, S ^{[1
]}

Gelpi, A ^{[1
]}

Takenouti, H ^{[1
]}

Keddam, M ^{[1
]}

机构：

[1] FRAMATOME, Ctr Tech, F-71205 Le Creusot, France

来源：

PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS | 1999年

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Previous work on steam generator (SG) tubes pulled from French plants and laboratory simulations has shown that corrosion in the secondary side of the SG occurs under alumino-silicate or aluminate deposits. The analyses of surface reactions showed that iron and nickel migrate from inside the alumino-silicate deposit while chromium is located as hydroxide in a non-protective layer below the deposits. In the presence of carboxylic compounds, chromium can also migrate inside this alumino-silicate layer. Laboratory experiments with impedance measurements (EIS) confirmed the fact that two media, silica with organic species and phosphate with organic species are able to produce IGA especially under polarization. EIS technique can detect the IGA formation in situ in aqueous media at high temperatures by the change in diffusion response. This occurs under cathodic polarization, which modifies the behavior of the organic compound. Electrochemical tests and FTIR analyses explain the transformation of the organic compounds.

引用

页码：587 / 597

页数：11

共 50 条

[11] GALVANIC-CREVICE CORROSION IN THE SECONDARY ENVIRONMENT OF NUCLEAR STEAM-GENERATORS
MCKUBRE, MCH
LEACH, SC
SHOEMAKER, CE
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (8B) : C423 - C423
[12] Safety and availability of steam generator tubes affected by secondary side corrosion
Dvorsek, T
Cizelj, L
Mavko, B
NUCLEAR ENGINEERING AND DESIGN, 1998, 185 (01) : 11 - 21
[13] CORROSION OF PWR STEAM-GENERATORS
GARNSEY, R
NUCLEAR ENERGY-JOURNAL OF THE BRITISH NUCLEAR ENERGY SOCIETY, 1979, 18 (02): : 117 - 132
[14] CORROSION OF PWR STEAM GENERATORS.
Garnsey, R.
Nuclear Energy, 1979, 18 (02): : 117 - 132
[15] Corrosion types specific for steam generators
Lucan, D
Pirvan, I
Radulescu, M
Fulger, M
Jinescu, G
REVISTA DE CHIMIE, 1997, 48 (10-11): : 905 - 909
[16] Calculation model for 16N transit time in secondary side of steam generators
Liu, Songyu
Xu, Jijun
Xu, Ming
Hedongli Gongcheng/Nuclear Power Engineering, 1998, 19 (02): : 106 - 110
[17] CREVICE CORROSION OF LATTICE SUPPORT ALLOYS IN SECONDARY ENVIRONMENTS OF NUCLEAR STEAM GENERATORS.
McKubre, M.C.H.
Leach, S.C.
Eiselstein, L.E.
Shoemaker, C.E.
Electric Power Research Institute (Report) EPRI NP, 1983,
[18] STEAM SIDE WATER CHEMISTRY IN PWR STEAM-GENERATORS
SAMUEL, T
TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1975, 20 (APR21): : 195 - 196
[19] ASSESSMENT OF WATER-SIDE CORROSION PROBLEMS IN FERRITIC STEEL LMFBR STEAM-GENERATORS
ISAACS, HS
TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1974, 18 (JUN23): : 116 - 117
[20] CORROSION OF FOSSIL FUELED STEAM-GENERATORS
KLEIN, HA
COMBUSTION, 1973, 44 (07): : 5 - 20

← 1 2 3 4 5 →