Atmospheric chloride-induced stress corrosion cracking of laser engraved type 316L stainless steel

被引：17
|
作者：
Krawczyk, Benjamin [1 ]
Cook, Paul [2 ]
Hobbs, Jeff [2 ]
Engelberg, Dirk L. [1 ]
机构：
[1] Univ Manchester, Sch Mat, Corros & Protect Ctr, Manchester, Lancs, England
[2] Sellafield Ltd, Seascale CA28 7PB, Gumbria, England
来源：
CORROSION SCIENCE | 2018年 / 142卷
关键词：
Austenitic stainless steel; Laser engraving; Laser marking; Tensile residual stress; Aqua blasting; Residual stress; SCC; Stress corrosion cracking; Atmospheric corrosion; RESIDUAL-STRESS; PITTING CORROSION; WASTE CONTAINERS; PART; RESISTANCE; MICROSTRUCTURE; IRRADIATION; DEPOSITS; 304-STAINLESS-STEEL; SURFACES;
D O I：
10.1016/j.corsci.2018.07.016
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influence of aqua blasting and laser engraving on the atmospheric chloride-induced stress corrosion cracking (AISCC) resistance of type 316 L stainless steel has been elucidated by using MgCl2-laden droplet deposits as the test medium. Aqua blasted surfaces showed no evidence of AISCC. Laser engraving resulted in tensile residual stresses, and led to AISCC within two weeks of exposure, with crack growth rates similar to U-bend samples. Introducing compressive residual stresses via peening inhibited crack nucleation, whereas oxide layer removal of engraved surfaces had no effect on AISCC. Strategies to reduce the likelihood of AISCC of laser engraved components are discussed.
引用
收藏
页码：93 / 101
页数：9
相关论文
共 50 条
  • [31] The initiation and propagation of chloride-induced transgranular stress-corrosion cracking (TGSCC) of 304L austenitic stainless steel under atmospheric conditions
    Spencer, D. T.
    Edwards, M. R.
    Wenman, M. R.
    Tsitsios, C.
    Scatigno, G. G.
    Chard-Tuckey, P. R.
    CORROSION SCIENCE, 2014, 88 : 76 - 88
  • [32] Chloride-induced stress corrosion cracking of used nuclear fuel welded stainless steel canisters: A review
    Xie, Yi
    Zhang, Jinsuo
    JOURNAL OF NUCLEAR MATERIALS, 2015, 466 : 85 - 93
  • [33] Cracking Mechanism of Laser Cladding Rapid Manufacturing 316L Stainless Steel
    Song Jian-li
    Li Yong-tang
    Deng Qi-lin
    Cheng, Z. -Y.
    Chin, Bryan
    ADVANCED DESIGN AND MANUFACTURE II, 2010, 419-420 : 413 - +
  • [34] Chloride-induced stress corrosion cracking of powder metallurgy duplex stainless steels
    Laitinen, A
    Hanninen, H
    CORROSION, 1996, 52 (04) : 295 - 306
  • [35] Chloride-induced alterations of the passive film on 316L stainless steel and blocking effect of pre-passivation
    Wang, Zuocheng
    Seyeux, Antoine
    Zanna, Sandrine
    Maurice, Vincent
    Marcus, Philippe
    ELECTROCHIMICA ACTA, 2020, 329
  • [36] Stress corrosion cracking on irradiated 316 stainless steel
    Furutani, G
    Nakajima, N
    Konishi, T
    Kodama, M
    JOURNAL OF NUCLEAR MATERIALS, 2001, 288 (2-3) : 179 - 186
  • [37] Stress-Corrosion Cracking of AISI 316L Stainless Steel in Seawater Environments: Effect of Surface Machining
    Ren, Zhe
    Ernst, Frank
    METALS, 2020, 10 (10) : 1 - 17
  • [38] Stress Corrosion Cracking of 316L Stainless Steel Additively Manufactured with Sinter-Based Material Extrusion
    Santamaria, Ricardo
    Wang, Ke
    Salasi, Mobin
    Iannuzzi, Mariano
    Mendoza, Michael Y.
    Quadir, Md Zakaria
    MATERIALS, 2023, 16 (11)
  • [39] Biaxial stress corrosion cracking of 316L stainless steel in MgCl2 (44%) at 154°C
    Farre, M.T.
    Andrieu, E.
    Pilvin, P.
    Vancon, D.
    Annales de Chimie: Science des Materiaux, 24 (4-5): : 313 - 319
  • [40] Stress Corrosion Cracking Behavior of Austenitic Stainless Steel 316L Produced Using Laser-Based Powder Bed Fusion
    Santamaria, Ricardo
    Wang, Ke
    Salasi, Mobin
    Salem, Mehdi
    Lours, Philippe
    Iannuzzi, Mariano
    Quadir, Md Zakaria
    CORROSION, 2023, 79 (08) : 944 - 956
12345