Wear resistance of TiN coatings implanted with Al and N ions

被引:11
|
作者
Naroiczyk, Jerzy
Werner, Zbigniew [1 ]
Morozow, Dmitrij
Tuszynski, Waldemar
机构
[1] Andrzej Soltan Inst Nucl Studies, PL-05400 Otwock, Poland
[2] Tech Univ Radom, PL-26600 Radom, Poland
[3] Inst Phys Chem PAS, PL-01224 Warsaw, Poland
[4] Inst Terotechnol, PL-26600 Radom, Poland
关键词
aluminium ion implantation; TiN coating;
D O I
10.1016/j.vacuum.2007.01.022
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Titanium nitride (TiN) coatings were prepared on HS 6-5-2 high-speed steel cutting inserts and next implanted either with Al ions (fluence 2 x 10(17) ions/cm(2)) or with Al and N ions (fluence (1 + 1) x 10(17) ions/cm(2)) on the rake face. Microhardness and friction coefficient of the implanted surfaces were examined. A noticeable increase of microhardness in Al implanted inserts has been observed. The elemental composition and structural properties of the surface layer were examined by glow discharge optical emission spectroscopy (GDOES) and gliding angle X-ray diffraction (XRD). The tests of turning of 40 H constructional steel with the cutting inserts have shown an improvement in the implanted inserts, especially marked in those implanted with Al + N. (c) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码:1275 / 1277
页数:3
相关论文
共 50 条
  • [21] THICK TI/TIN MULTILAYERED COATINGS FOR ABRASIVE AND EROSIVE WEAR-RESISTANCE
    LEYLAND, A
    MATTHEWS, A
    SURFACE & COATINGS TECHNOLOGY, 1994, 70 (01): : 19 - 25
  • [22] The tin stabilization effect on the microstructure, corrosion and wear resistance of electroless NiB coatings
    Bonin, L.
    Vitry, V.
    Delaunois, F.
    SURFACE & COATINGS TECHNOLOGY, 2019, 357 : 353 - 363
  • [23] Optimum multilayer TiN-TiCN coatings for wear resistance and actual application
    Su, YL
    Kao, WH
    WEAR, 1998, 223 (1-2) : 119 - 130
  • [24] Wear Resistance of the Coatings of Fe–Cr–Мn–Ti–Al System Sprayed from Powder Wires
    L. І. Bohun
    T. М. Kovbasyuk
    V. І. Kushpir
    I. А. Humenyuk
    Materials Science, 2019, 55 : 225 - 231
  • [25] Erosion and Abrasion Resistance, Mechanical Properties, and Structure of the TiN, Ti–Cr–Al–N and Cr–Al–Ti–N Coatings Deposited by CFUBMS
    Ph. V. Kiryukhantsev-Korneev
    J. Phiri
    V. I. Gladkov
    S. N. Ratnikov
    M. G. Yakovlev
    E. A. Levashov
    Protection of Metals and Physical Chemistry of Surfaces, 2019, 55 : 913 - 923
  • [26] Mechanical properties of (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings
    Chen, Li
    Du, Yong
    Yin, Fei
    Li, Jia
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2007, 25 (01): : 72 - 76
  • [27] Microstructure and wear resistance of thermal sprayed steel coatings ion beam implanted with nitrogen
    Byeli, Alexey V.
    Belotserkovskii, Marat A.
    Kukareko, Vladimir A.
    WEAR, 2009, 267 (9-10) : 1757 - 1761
  • [28] XPS study of vapour deposited wear-resistant coatings implanted with nitrogen and carbon ions
    Stock, HR
    Berndt, H
    Hohl, F
    Seidel, F
    Mayr, P
    ION BEAM MODIFICATION OF MATERIALS, 1996, : 1028 - 1033
  • [29] Solid solution hardening in nanolaminate ZrN-TiN coatings with enhanced wear resistance
    Herrera-Jimenez, E. J.
    Raveh, A.
    Schmitt, T.
    Bousser, E.
    Klemberg-Sapieha, J. E.
    Martinu, L.
    THIN SOLID FILMS, 2019, 688
  • [30] Effect of ion bombardment and micro -blasting on the wear resistance properties of hard TiN coatings
    Mundotia, R.
    Kothari, D. C.
    Kale, A.
    Mhatre, U.
    Date, K.
    Thorat, N.
    Ghorude, T.
    MATERIALS TODAY-PROCEEDINGS, 2020, 26 : 603 - 612