Single and multi domain buckled germanene phases on Al(111) surface

The simultaneous formation of single domain (3x3) and multi domain (root 7x root 7)R(+/- 19.1 degrees) germanene phases on Al(111) surface in the sub-monolayer range was studied using scanning tunneling microscopy (STM) and density functional theory (DFT) based simulations. Experimental results revealed that both germanene phases nucleate and grow independently from each other and regardless of Al substrate temperature within significantly expanded range T-s = 27-200 degrees C. Our results unambiguously showed that STM images with hexagonal contrast yield correct-resolved structure for both germanene phases, while honeycomb contrast is a result of an artificial tip-induced STM resolution. First-principles calculations suggested atomic models with strongly buckled germanene (2x2)/Al(111)(3x3) and (root 3x root 3)R30 degrees/Al(111)(root 7x root 7)R(+/- 19.1 degrees) with one of eight and one of six Ge atoms protruding upward respectively, that consistently describe the experimentally observed STM images both for single and multi domain surface phases. According to the DFT based simulations both germanene (2x2) and (root 3x root 3)R30 degrees superstructures have a stretched lattice strain with respect to the ideal free-standing germanene by 6.2% and 13.9%, respectively. Hence, numerous small domains separated by domain boundaries in the (root 3x root 3)R307Al(111)(root 7x root 7)R(+/- 19.1 degrees) germanene phase tend to reduce the surface energy and prevent the formation of extended single domains, in contrast to the (2x2)/Al(111)(3x3) phase. However, our experimental results showed that the nucleation and growth of germanene on Al(111) surface yield strong modifications of Al surface even at room temperature (RT), which may be contributed to the formation of Al-Ge alloy due to Ge surface solid-states reactivity that was ignored in recent studies. It is already evident from our present findings that the role of Al atoms in the formation of (3x3) and (root 7x root 7)R(+/- 19.1 degrees) germanene phases is worthy to be carefully studied in the future, which could be an important knowledge for large-quantity fabrication of germanene on aluminum.