Failure analysis of a natural gas pipeline

被引：15
|
作者：
Zhao, Yafan [1 ]
Song, Mingda [2 ]
机构：
[1] Shandong Jianzhu Univ, Jinan 250014, Peoples R China
[2] Shandong Special Equipment Inspect Inst, Jinan 250013, Peoples R China
来源：
ENGINEERING FAILURE ANALYSIS | 2016年 / 63卷
关键词：
Natural gas pipeline; SCC; Mechanical damage; Failure analysis;
D O I：
10.1016/j.engfailanal.2016.02.023
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A L390 natural gas pipeline exploded in 2011 in China. Macrofracture examination, thickness measurement, chemical composition analysis, metallographic inspection, mechanical property testing, fracture scan electronic microscopy examination and environment analysis were conducted to the burst pipeline. The results showed that Stress Corrosion Cracking (SCC) generated in the mechanical damaged zone of the pipeline was the reason of the failure. This kind of cracking was induced by Cl- and HCO3- in near neutral corrosive medium of pH value. The stress concentration was induced by the groove damage under inner pressure. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：61 / 71
页数：11
相关论文
共 50 条
  • [31] Failure of a Squeeze-Clamped Polyethylene Natural Gas Pipeline
    Jones, Robert E., Jr.
    Bradley, Walter L.
    [J]. JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2022, 22 (05) : 2023 - 2029
  • [32] Failure of a Squeeze-Clamped Polyethylene Natural Gas Pipeline
    Robert E. Jones
    Walter L. Bradley
    [J]. Journal of Failure Analysis and Prevention, 2022, 22 : 2023 - 2029
  • [33] Influence of hydrogen blending in natural gas pipeline on natural gas analysis and measurement
    Zhang P.
    Zhou L.
    Zhang P.
    Luo Q.
    Pu C.
    [J]. Natural Gas Industry, 2023, 43 (08) : 135 - 145
  • [34] Integrated failure probability estimation based on structural integrity analysis and failure data: Natural gas pipeline case
    Dundulis, Gintautas
    Zutautaite, Inga
    Janulionis, Remigijus
    Uspuras, Eugenijus
    Rimkevicius, Sigitas
    Eid, Mohamed
    [J]. RELIABILITY ENGINEERING & SYSTEM SAFETY, 2016, 156 : 195 - 202
  • [35] Risk Analysis of Natural Gas Pipeline: Case Study of a Generic Pipeline
    Vianello, Chiara
    Maschio, Giuseppe
    [J]. ICHEAP-10: 10TH INTERNATIONAL CONFERENCE ON CHEMICAL AND PROCESS ENGINEERING, PTS 1-3, 2011, 24 : 1309 - 1314
  • [36] Failure analysis of CO2 corrosion of natural gas pipeline under flowing conditions
    Li, Jiahang
    Wang, Dan
    Xie, Fei
    [J]. ENGINEERING FAILURE ANALYSIS, 2022, 137
  • [37] Failure analysis of CO2 corrosion of natural gas pipeline under flowing conditions
    Li, Jiahang
    Wang, Dan
    Xie, Fei
    [J]. Engineering Failure Analysis, 2022, 137
  • [38] A bibliometric analysis on oil and gas pipeline failure consequence analysis
    Armin Aalirezaei
    Golam Kabir
    [J]. Innovative Infrastructure Solutions, 2021, 6
  • [39] A bibliometric analysis on oil and gas pipeline failure consequence analysis
    Aalirezaei, Armin
    Kabir, Golam
    [J]. INNOVATIVE INFRASTRUCTURE SOLUTIONS, 2021, 6 (04)
  • [40] Investigation of different failure modes in oil and natural gas pipeline steels
    Pourazizi, Reza
    Mohtadi-Bonab, M. A.
    Szpunar, J. A.
    [J]. ENGINEERING FAILURE ANALYSIS, 2020, 109
12345