Corrosion-Fatigue Performance of Hard Anodized and MAO-Coated 2024-T3 and 7075-T6 Aerospace Al Alloys

被引：7
|
作者：
Madhavi, Y. [1 ,2 ]
Krishna, Rama L. [1 ]
Narasaiah, N. [1 ]
机构：
[1] Int Adv Res Ctr Powder Met & New Mat ARCI, Ctr Engn Coatings, Hyderabad, India
[2] Natl Inst Technol NIT, Met & Mat Engn, Warangal, Andhra Pradesh, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2021年 / 74卷 / 09期
关键词：
Plasma electrolytic oxidation; Impedance; Polarization; High cycle fatigue; Shot peening; Micro-arc oxidation; MICRO ARC OXIDATION; ALUMINUM-ALLOY; PEO TREATMENT; COATINGS; BEHAVIOR; LIFE;
D O I：
10.1007/s12666-021-02313-7
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
In the present study, micro-arc oxidation (MAO) coatings were deposited on shot peened high-strength aerospace aluminium alloys namely 2024-T3 and 7075-T6. The comparative corrosion-fatigue performance was evaluated in 3.5 wt.% NaCl corrosion environment for bare, hard anodized and SP + MAO (prior shot-peened and MAO) coated Al alloys. Also, the corrosion behavior of bare and SP + MAO coated Al alloys was assessed through potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) tests. In addition, SP + MAO coatings were characterized for the phase composition, surface/cross-sectional morphologies and surface roughness. Furthermore, the corrosion-fatigue fractured features of coatings were examined to understand the failure mechanisms. The SP + MAO coatings deposited on Al alloys possess superior corrosion-fatigue life as compared to the bare and hard anodized conditions.
引用
收藏
页码：2231 / 2243
页数：13
相关论文
共 50 条
  • [21] An analytical electron microscopy study of constituent particles in commercial 7075-T6 and 2024-T3 alloys
    Gao, M
    Feng, CR
    Wei, RP
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (04): : 1145 - 1151
  • [22] An analytical electron microscopy study of constituent particles in commercial 7075-T6 and 2024-T3 alloys
    Ming Gao
    C. R. Feng
    Robert P. Wei
    Metallurgical and Materials Transactions A, 1998, 29 : 1145 - 1151
  • [23] Local melting and cracking in Al 7075-T6 and Al 2024-T3 friction stir spot welds
    Gerlich, A.
    Yamamoto, M.
    North, T. H.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2007, 12 (06) : 472 - 480
  • [24] Corrosion-fatigue behavior of welded aluminum alloy 2024-T3
    Yadav, V. K.
    Gaur, V.
    Singh, I. V.
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 173
  • [25] Corrosion-fatigue crack nucleation in Al clad 2024-T3 commercial aircraft skin
    Schmidt, CG
    Crocker, JE
    Giovanola, JH
    Kanazawa, CH
    Shockey, DA
    Flournoy, TH
    EFFECTS OF THE ENVIRONMENT ON THE INITIATION OF CRACK GROWTH, 1997, 1298 : 74 - 88
  • [26] Test environment selection for corrosion-fatigue testing of aluminum alloy 7075-T6
    Ciccone, MP
    Gangloff, RP
    Kelly, RG
    CORROSION, 2005, 61 (06) : 571 - 578
  • [27] Effect of single tensile peak overload on the performance of bonded composite repair of cracked Al 2024-T3 and Al 7075-T6 plates
    Mohammed, Sohail M. A. Khan
    Albedah, A.
    Benyahia, F.
    Bouiadjra, B. Bachir
    COMPOSITE STRUCTURES, 2018, 193 : 260 - 267
  • [28] INFLUENCE OF DIFFERENT TYPES OF ANODIC LAYERS ON THE FATIGUE PROPERTIES OF 2024-T3 AND 7075-T6 SHEET MATERIAL.
    't Hart, W.G.J.
    Nederveen, A.
    1600,
  • [29] EFFECTS OF PRECRACK DAMAGE ON THE RATE OF CRACK-PROPAGATION IN 2024-T3 AND 7075-T6 ALUMINUM-ALLOYS
    JOSHI, NR
    MIRMIRAN, SGR
    MATERIALS EVALUATION, 1979, 37 (10) : P4 - P4
  • [30] Probabilistic fatigue crack growth assessment of Al 7075-T6 aerospace component
    Bahloul, Ahmed
    Ben Ahmed, Amal
    Bouraoui, Chokri
    2ND INTERNATIONAL CONFERENCE ON STRUCTURAL INTEGRITY, ICSI 2017, 2017, 5 : 430 - 437
12345