Influence of oxide film on weld characteristics of mild steel in CO2 laser welding

被引：0

作者：

Ono, K ^{[1
]}

Adachi, K ^{[1
]}

Matsumoto, Y ^{[1
]}

Miyamoto, I ^{[1
]}

Inoue, T ^{[1
]}

Narita, R ^{[1
]}

机构：

[1] KOMATSU Ltd, Mfg Engn Dev Ctr, Hirakata, Osaka 5731011, Japan

来源：

ICALEO (R)'99: PROCEEDING OF THE LASER MATERIALS PROCESSING CONFERENCE, VOL 87, PTS 1 AND 2 | 2000年 / 87卷

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Influence of oxide film, such as laser cutting edges or mill scale, on weld characteristics of mild steel in CO2 laser welding was investigated. Autogenous laser welding tests with oxidized face of joint were carried out. A lot of spatters were observed during welding operation and therefore the top of bead was underfilled and irregular. Bead width of surface was reduced and side walls of weld metal were nearly parallel. In microstructure, ferrite on gamma grain boundary and ferrite side plate were larger and vickers hardness was lower. Porosity consisted of CO, CO2, H-2 and sometime He were generated. Reason of the result was discussed in this paper with observation of laser induced plasma and comparing with Electron Beam Welding.

引用

页码：D83 / D91

页数：3

共 50 条

[41] Multi-criteria assessment of process performance characteristics in CO2 laser cutting of mild steel
Madić, Miloš
Radovanović, Miroslav
Petković, Dušan
Nedić, Bogdan
[J]. Academic Journal of Manufacturing Engineering, 2015, 13 (02): : 6 - 11
[42] Experimental study on welding characteristics of CO2 laser TIG hybrid welding process
Chen, Y. B.
Lei, Z. L.
Li, L. Q.
Wu, L.
[J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2006, 11 (04) : 403 - 411
[43] Contact mechanical studies on continuous wave CO2 laser beam weld of mild steel with ambient and under water medium
Kumar, N.
Kataria, S.
Shanmugarajan, B.
Dash, S.
Tyagi, A. K.
Padmanabham, G.
Raj, Baldev
[J]. MATERIALS & DESIGN, 2010, 31 (08) : 3610 - 3617
[44] Comparative study on CO2 laser overlap welding and resistance spot welding for galvanized steel
Mei Lifang
Yi Jiming
Yan Dongbing
Liu Jinwu
Chen Genyu
[J]. MATERIALS & DESIGN, 2012, 40 : 433 - 442
[45] Blue-Light Hazard from CO2 Arc Welding of Mild Steel
Okuno, T.
Ojima, J.
Saito, H.
[J]. ANNALS OF OCCUPATIONAL HYGIENE, 2010, 54 (03): : 293 - 298
[46] CUTTING AND WELDING WITH CO2 LASER
不详
[J]. METAL FORMING, 1969, 36 (09): : 258 - &
[47] Chemistry and Structure of the Passive Film on Mild Steel in CO2 Corrosion Environments
Han, Jiabin
Young, David
Colijn, Hendrik
Tripathi, Akhilesh
Nesic, Srdjan
[J]. INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2009, 48 (13) : 6296 - 6302
[48] Influence of the wire addition direction in CO2 laser welding of aluminum
Xiao, RS
Chen, K
Zuo, TC
Ambrosy, G
Hügel, H
[J]. LASERS IN MATERIAL PROCESSING AND MANUFACTURING, 2002, 4915 : 128 - 137
[49] Characteristics of CO2 Laser Welded TRIP Steel Sheet
Wang, Wenquan
Huang, Shiming
You, Qun
Kang, C. Y.
[J]. MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5, 2011, 189-193 : 3764 - +
[50] Analysis of mechanism of plasma and spatter in CO2 laser welding of galvanized steel
Park, H
Rhee, S
[J]. OPTICS AND LASER TECHNOLOGY, 1999, 31 (02): : 119 - 126

← 1 2 3 4 5 →