Exfoliation corrosion behavior of 7050-T6 aluminum alloy treated with various quench transfer time

被引：43
|
作者：
Song, Feng-xuan [1 ]
Zhang, Xin-ming [1 ]
Liu, Sheng-dan [1 ]
Tan, Qi [1 ]
Li, Dong-feng [1 ]
机构：
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2014年 / 24卷 / 07期
关键词：
7050-T6 aluminum alloy; thick plate; exfoliation corrosion; quench transfer time; electrochemistry; MG-CU ALLOYS; MECHANICAL-PROPERTIES; MICROSTRUCTURES;
D O I：
10.1016/S1003-6326(14)63342-2
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The exfoliation corrosion (EFC) behavior of 7050-T6 aluminum alloy treated with various quench transfer time after solution heat treatment was investigated by standard EFC immersion tests, strength loss measurements after EFC tests and electrochemical impedance spectroscope (EIS) technique. The results showed that EFC resistance of the alloy decreased with increasing quench transfer time. Backscattered electron scanning electron microscope (SEM) together with transmission electron microscope (TEM) observations revealed that the coverage ratio and microstructure of precipitates at grain boundary area are the most important factors which influence the EFC susceptibility of the alloy, while precipitate-free zone (PFZ) near grain boundary has no or only a minor effect on it. In addition, galvanostatic measurements of the alloy present a good correlation between EFC resistance and transients in potential. The cumulated number of transients in potential can be used to evaluate EFC resistance of the alloy.
引用
收藏
页码：2258 / 2265
页数：8
相关论文
共 50 条
  • [21] Effects of step-quench and aging on mechanical properties and resistance to stress corrosion cracking of 7050 aluminum alloy
    Ou, BL
    Yang, JG
    Yang, CK
    MATERIALS TRANSACTIONS JIM, 2000, 41 (07): : 783 - 789
  • [22] Fitting corrosion and fatigue behavior of aluminum alloy 7075-T6
    Sankaran, KK
    Perez, R
    Jata, KV
    ADVANCED MATERIALS & PROCESSES, 2000, 158 (02): : 53 - 54
  • [23] Effect of tensile pre-strain on low-cycle fatigue behaviour of 7050-T6 aluminium alloy
    Branco, R.
    Costa, J. D.
    Borrego, L. P.
    Wu, S. C.
    Long, X. Y.
    Antunes, F., V
    ENGINEERING FAILURE ANALYSIS, 2020, 114
  • [24] Study on hydrogen-assisted stress corrosion cracking behavior of 7050 aluminum alloy
    Zhang, Qiang
    Shao, Shanshan
    Huang, Yuhui
    Tu, Shan-Tung
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2025, 35 : 6184 - 6197
  • [25] Influence of quench delay time on the corrosion behavior of aluminium alloy 2024
    Campestrini, P
    van Rooijen, HW
    van Westing, EPM
    de Wit, JHW
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2000, 51 (09): : 616 - 627
  • [26] Study of anodizing behavior and corrosion resistance of 7050 T7451 alloy
    Zhang, Q
    Wang, W
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 280 (01): : 168 - 172
  • [27] Corrosion and passivation behavior of 6082-T6 aluminum alloy in NaCl solution
    Yang, Li
    Bai, Di
    Zhang, Chi
    Yang, Shoubing
    Wang, Dongxu
    Liu, Chaojie
    Ge, Tianqi
    Huang, Genzhe
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2023, 74 (04): : 622 - 629
  • [28] CORROSION BEHAVIOR OF A WC/C COATED 7075-T6 ALUMINUM ALLOY
    Baragetti, S.
    Dauru, M.
    Gerosa, R.
    Rivolta, B.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII, 2014, 577-578 : 217 - +
  • [29] Corrosion Behavior of 7075-T6 Aluminum Alloy in the Presence of Aspergillus Niger
    Fan, Qi
    Fu, Lei
    Lin, Li
    Lai, Sheng
    Huang, Xin Jie
    Zhang, Yingqian
    Luo, Yunrong
    Li, Xiulan
    Zhang, HaiZhou
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (09): : 1 - 16
  • [30] Exfoliation corrosion of T6- and T8-aged AlxCuyLiz alloy
    李红英
    唐宜
    曾再得
    郑峰
    Transactions of Nonferrous Metals Society of China, 2008, (04) : 778 - 783
12345