Exfoliation corrosion behavior of 7050-T6 aluminum alloy treated with various quench transfer time

被引：43
|
作者：
Song, Feng-xuan [1 ]
Zhang, Xin-ming [1 ]
Liu, Sheng-dan [1 ]
Tan, Qi [1 ]
Li, Dong-feng [1 ]
机构：
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2014年 / 24卷 / 07期
关键词：
7050-T6 aluminum alloy; thick plate; exfoliation corrosion; quench transfer time; electrochemistry; MG-CU ALLOYS; MECHANICAL-PROPERTIES; MICROSTRUCTURES;
D O I：
10.1016/S1003-6326(14)63342-2
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The exfoliation corrosion (EFC) behavior of 7050-T6 aluminum alloy treated with various quench transfer time after solution heat treatment was investigated by standard EFC immersion tests, strength loss measurements after EFC tests and electrochemical impedance spectroscope (EIS) technique. The results showed that EFC resistance of the alloy decreased with increasing quench transfer time. Backscattered electron scanning electron microscope (SEM) together with transmission electron microscope (TEM) observations revealed that the coverage ratio and microstructure of precipitates at grain boundary area are the most important factors which influence the EFC susceptibility of the alloy, while precipitate-free zone (PFZ) near grain boundary has no or only a minor effect on it. In addition, galvanostatic measurements of the alloy present a good correlation between EFC resistance and transients in potential. The cumulated number of transients in potential can be used to evaluate EFC resistance of the alloy.
引用
收藏
页码：2258 / 2265
页数：8
相关论文
共 50 条
  • [1] The effect of quench transfer time on microstructure and localized corrosion behavior of 7050-T6 Al alloy
    Song, F. X.
    Zhang, X. M.
    Liu, S. D.
    Tan, Q.
    Li, D. F.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2014, 65 (10): : 1007 - 1016
  • [2] Low-Cycle Fatigue and Ratcheting Lifetime Estimation of a 7050-T6 Aluminum Alloy
    L. Fu
    H. Duan
    Q. Y. Wang
    J. Yao
    L. Lin
    Y. Q. Zhang
    Y. R. Luo
    Strength of Materials, 2020, 52 : 596 - 606
  • [3] Low-Cycle Fatigue and Ratcheting Lifetime Estimation of a 7050-T6 Aluminum Alloy
    Fu, L.
    Duan, H.
    Wang, Q. Y.
    Yao, J.
    Lin, L.
    Zhang, Y. Q.
    Luo, Y. R.
    STRENGTH OF MATERIALS, 2020, 52 (04) : 596 - 606
  • [4] Quench sensitivity relative to exfoliation corrosion of 7085 aluminum alloy
    Zhang, X. (xmzhang@mail.csu.edu.cn), 1600, Chinese Journal of Materials Research (27):
  • [5] Mechanisms of fatigue crack growth in 7050-T6 aluminium alloy
    Borrego, L. P.
    Jesus, J. S.
    Branco, R.
    Ferreira, J. A. M.
    Antunes, F. V.
    Neto, D. M.
    Sergio, E. R.
    INTERNATIONAL JOURNAL OF FATIGUE, 2025, 194
  • [6] Research on Microstructure and Fatigue Properties of 7050-T6 High-Strength Aluminum Alloy Cold Metal Transfer Welded Joint
    Zhu, Minqi
    Yang, Shanglei
    Xie, Chaojie
    Bai, Yishan
    Fan, Cong
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (10) : 7461 - 7471
  • [7] Research on Microstructure and Fatigue Properties of 7050-T6 High-Strength Aluminum Alloy Cold Metal Transfer Welded Joint
    Minqi Zhu
    Shanglei Yang
    Chaojie Xie
    Yishan Bai
    Cong Fan
    Journal of Materials Engineering and Performance, 2021, 30 : 7461 - 7471
  • [8] Exfoliation corrosion behavior of 2524 aluminum alloy
    Yang, Sheng
    Yl, Danqing
    Yao, Sujuan
    Hou, Yaping
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 1159 - +
  • [9] Fatigue crack growth modelling based on CTOD for the 7050-T6 alloy
    Antunes, F. V.
    Branco, R.
    Prates, P. A.
    Borrego, L.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (08) : 1309 - 1320
  • [10] Effect of strain ratio on cyclic deformation behaviour of 7050-T6 aluminium alloy
    Branco, R.
    Costa, J. D.
    Borrego, L. P.
    Wu, S. C.
    Long, X. Y.
    Zhang, F. C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 129
12345