Prediction of long-term creep-fatigue life of stainless steel weldment based on microstructure degradation

被引：0
|
作者：
Asayama, T [1 ]
Hasebe, S [1 ]
机构：
[1] POWER REACTOR & NUCL FUEL DEV CORP,OARAI ENGN CTR,OARAI,IBARAKI 31113,JAPAN
来源：
MATERIALS SCIENCE RESEARCH INTERNATIONAL | 1997年 / 3卷 / 03期
关键词：
stainless steel weld metal; degradation of microstructure; creep-fatigue;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This paper describes a newly developed analytical method for the evaluation of creep-fatigue strength for stainless weld metal. Based on the observation that creep-fatigue crack initiated adjacent to the interface of sigma-phase/delta-ferrite and matrix, a mechanical model, which allowed the evaluation of micro stress/strain concentration adjacent to the interface, was developed. Fatigue and creep damages were evaluated, using the model which described the microstructure after long time exposure to high temperatures. It is concluded that one major scope of this model is to predict analytically long term creep/fatigue life of stainless steel weld metals, the microstructure of which has been degraded as a result of in-service high temperature exposure.
引用
收藏
页码：171 / 177
页数：7
相关论文
共 50 条
  • [21] Creep-fatigue life prediction of G91 steel based on mechanistic model
    Yaguchi, M
    Asada, Y
    SIXTH INTERNATIONAL CONFERENCE ON CREEP AND FATIGUE: DESIGN AND LIFE ASSESSMENT AT HIGH TEMPERATURE, 1996, 1996 (02): : 193 - 201
  • [22] Long-term creep life prediction for a high chromium steel
    Wilshire, B.
    Scharning, P. J.
    SCRIPTA MATERIALIA, 2007, 56 (08) : 701 - 704
  • [23] EVALUATION METHOD OF CREEP-FATIGUE LIFE FOR 316FR WELDMENT
    Nagae, Yuji
    Yamamoto, Kenji
    Otani, Tomomi
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 6A, 2015,
  • [24] The Unified Creep-Fatigue Equation for Stainless Steel 316
    Liu, Dan
    Pons, Dirk John
    Wong, Ee-hua
    METALS, 2016, 6 (09)
  • [25] Effect of ratcheting deformation on fatigue and creep-fatigue life of 316FR stainless steel
    Date, Shingo
    Ishikawa, Hiroshi
    Otani, Tomorni
    Takahashi, Yukio
    NUCLEAR ENGINEERING AND DESIGN, 2008, 238 (02) : 336 - 346
  • [26] Assessment of damage and life prediction of austenitic stainless steel under high temperature creep-fatigue interaction condition
    Nam, SW
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 322 (1-2): : 64 - 72
  • [27] CREEP-FATIGUE BEHAVIOR AND LIFE PREDICTION OF 316L STAINLESS STEEL UNDER DIFFERENT LOADING LEVELS
    Jiang, Huifeng
    Chen, Xuedong
    Fan, Zhichao
    Dong, Jie
    Jiang, Heng
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 6, PTS A AND B, 2010, : 1445 - 1450
  • [28] Creep-fatigue life prediction based on a new damage rule
    Tokimasa, Katsuyuki
    Miyahara, Mitsuo
    Sumitomo Metals, 1996, 48 (02): : 20 - 29
  • [29] LIFE PREDICTION FOR CREEP-FATIGUE BASED ON THE GROWTH OF SHORT CRACKS
    RENNER, E
    VEHOFF, H
    NEUMANN, P
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1989, 12 (06) : 569 - 584
  • [30] Weld metal creep-fatigue life prediction by modeling the microstructure degradation due to the exposure to high temperature and load
    Asayama, T
    Hasebe, S
    NUCLEAR ENGINEERING AND DESIGN, 2000, 195 (02) : 197 - 210
12345