Effect of clay on the morphology of blends of poly(propylene) and polyamide 6/clay nanocomposites

PP/NPA6 blends composed of poly(propylene) (PP) and polyamide 6/clay nanocomposites (NPA6) were prepared by twin-screw extrusion and melt-drawn into ribbons by a ribbon extrusion process. The influence of clay on the morphology of PP/NPA6 ribbons was investigated by means of field-emission scanning electron microscopy and optical microscopy. The results show that at low clay content (3, 5 wt%), NPA6 exhibited continuous lamellar structure in PP as pristine PA6 did in a PP/PA6 blend, but at a higher clay content (10 wt%) only ellipsoids or elongated ellipsoids were observed. In order to explain the morphological difference, two factors, ie the compatibilization effect and melt theology, have been taken into consideration. It has been found that both factors, and probably mainly the variation in melt theology, were responsible for the morphological difference in the PP/NPA6 blends with different clay contents under the extensional flow field. (C) 2004 Society of Chemical Industry.