Localized corrosion of a 2219 aluminium alloy exposed to a 3.5% NaCl solution

被引：130
|
作者：
Grilli, Rossana [1 ]
Baker, Mark A. [1 ]
Castle, James E. [1 ]
Dunn, Barrie [2 ]
Watts, John F. [1 ]
机构：
[1] Univ Surrey, Fac Engn & Phys Sci, Surface Anal Lab, Surrey GU2 7XH, England
[2] European Space Technol Ctr, NL-2200 AG Noordwijk, Netherlands
来源：
CORROSION SCIENCE | 2010年 / 52卷 / 09期
关键词：
Aluminium alloy; Intermetallics; AES; Corrosion; PITTING CORROSION; INITIATION; SPECTROSCOPY; 2024-T3;
D O I：
10.1016/j.corsci.2010.04.035
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This work is focused on the role of intermetallics in pitting corrosion of Al2219 alloy. Second phase particles were characterized by AES, SAM and EDX. Their behaviour in a solution of NaCl was investigated as a function of exposure time. The results confirmed the cathodic nature of the intermetallics with respect to the aluminium matrix. Corrosion products rich in aluminium and oxygen were found to progressively accumulate around the particles and iron was dissolved from the intermetallic, followed by back-deposition. Copper and manganese did not show any major activity. After 32 h of exposure the larger intermetallics were completely covered. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2855 / 2866
页数：12
相关论文
共 50 条
  • [21] Galvanostatic response of AA2024 aluminium alloy in 3.5% NaCl solution
    Donatus, U.
    Thompson, G. E.
    BULLETIN OF MATERIALS SCIENCE, 2016, 39 (06) : 1537 - 1540
  • [22] Galvanostatic response of AA2024 aluminium alloy in 3.5% NaCl solution
    U DONATUS
    G E THOMPSON
    Bulletin of Materials Science, 2016, 39 : 1537 - 1540
  • [23] Corrosion behavior of WE54 magnesium alloy in 3.5%NaCl solution
    李卓群
    单大勇
    陈荣石
    柯伟
    韩恩厚
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (S3) : 1806 - 1809
  • [24] Corrosion behavior of WE54 magnesium alloy in 3.5%NaCl solution
    Li Zhuo-qun
    Shan Da-yong
    Chen Rong-shi
    Ke Wei
    Han En-hou
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S1806 - S1809
  • [25] Corrosion behavior of WE54 magnesium alloy in 3.5%NaCl solution
    Environmental Corrosion Center, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
    Trans Nonferrous Met Soc China, 2006, SUPPL. 3 (1806-1809):
  • [26] Mapping the fretting corrosion behaviors of 6082 aluminum alloy in 3.5% NaCl solution
    Pu, Jian
    Zhang, Yali
    Zhang, Xiaogang
    Yuan, Xinlu
    Ren, Pingdi
    Jin, Zhongmin
    WEAR, 2021, 482
  • [27] Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution
    Venugopal, A.
    Sreekumar, K.
    Raja, V. S.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (09): : 3135 - 3148
  • [28] Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution
    A. Venugopal
    K. Sreekumar
    V. S. Raja
    Metallurgical and Materials Transactions A, 2012, 43 : 3135 - 3148
  • [29] The electrochemical corrosion behaviour of quaternary gold alloys when exposed to 3.5 % NaCl solution
    L. P. Ward
    D. Chen
    A. P. O’Mullane
    Gold Bulletin, 2013, 46 : 35 - 45
  • [30] The electrochemical corrosion behaviour of quaternary gold alloys when exposed to 3.5 % NaCl solution
    Ward, L. P.
    Chen, D.
    O'Mullane, A. P.
    GOLD BULLETIN, 2013, 46 (01) : 35 - 45
12345