Influence of Nb addition on the oxidation behavior of novel Ni-base superalloy

被引：58
|
作者：
Ye, Xianjue [1 ]
Yang, Biaobiao [1 ]
Nie, Yan [1 ]
Yu, Shu [1 ]
Li, Yunping [1 ]
机构：
[1] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Peoples R China
来源：
CORROSION SCIENCE | 2021年 / 185卷
关键词：
Superalloy; Niobium; Oxidation; CrTaO4; HIGH-TEMPERATURE OXIDATION; CR-MO ALLOY; OXIDE-FILMS; RESISTANCE; KINETICS; AL; VOLATILIZATION; CRNBO4; GROWTH;
D O I：
10.1016/j.corsci.2021.109436
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Influence of Nb on oxidation behavior of novel Ni-base superalloy was investigated in detail at 1000 degrees C. Although alloy with 2 wt%Nb (2Nb) exhibits significantly higher weight gain than alloy without Nb (0Nb), oxide scale of 2Nb was more continuous and compact. In contrast, 0Nb underwent severe vaporization and spallation in oxide scale. Nb was found to accelerate the formation of compact TiO2 on Cr2O3 layer, leading to inhibited vaporization and spallation in oxide scale. Nb also accelerated the formation of continuous CrTaO4 layer beneath the Cr2O3, enhancing the oxidation resistance via inhibiting the interdiffusion of oxygen, nitrogen and metallic elements.
引用
收藏
页数：10
相关论文
共 50 条
  • [41] Isothermal Oxidation Behavior of a New Directionally Solidified Ni-base Superalloy in Air at Different Temperature
    Wang, Lei
    Huang, Yan
    Zhao, Zhuo
    Liu, Yang
    Wu, Jiantao
    Yan, Ping
    PRICM 7, PTS 1-3, 2010, 654-656 : 538 - +
  • [42] FRACTAL ANALYSES OF DIRECTIONAL SOLIDIFICATION BEHAVIOR OF A Ni-BASE SUPERALLOY
    SUN Liling DONG Lianke ZHANG Jishan TANG Yajun ZHANG Jinghua HU Zhuangqi Institute of Metal Research
    Acta Metallurgica Sinica(English Edition), 1993, (05) : 291 - 295
  • [43] Influence of heat treatment on the microstructure of a unidirectional Ni-base superalloy
    Huang, XB
    Kang, Y
    Zhou, HH
    Zhang, Y
    Hu, ZQ
    MATERIALS LETTERS, 1998, 36 (1-4) : 210 - 213
  • [44] Isothermal oxidation behaviour of a Ni-base superalloy at 900 and 1 000
    Shenyang Ligong University, Shenyang, China
    Gongneng Cailiao, 4 (04025-04030):
  • [45] Oxidation kinetics of cast Ni-base superalloy K35
    Li, Yun
    Yuan, Chao
    Guo, Jian-Ting
    Yang, Hong-Cai
    Dongbei Daxue Xuebao/Journal of Northeastern University, 2003, 24 (01): : 75 - 78
  • [46] Life prediction of a Ni-base superalloy
    Aghaie-Khafri, M.
    Noori, M.
    BULLETIN OF MATERIALS SCIENCE, 2011, 34 (02) : 305 - 309
  • [47] Life prediction of a Ni-base superalloy
    M AGHAIE-KHAFRI
    M NOORI
    Bulletin of Materials Science, 2011, 34 : 305 - 309
  • [48] Effect of Substrate Roughness on Oxidation Resistance of an Aluminized Ni-Base Superalloy
    Nowak, Wojciech J.
    Ochal, Kamil
    Wierzba, Patrycja
    Gancarczyk, Kamil
    Wierzba, Bartek
    METALS, 2019, 9 (07)
  • [49] Study of the Oxidation Assisted Intergranular Cracking Mechanism on a Ni-Base Superalloy
    Milanese, J.
    Andrieu, E.
    Osio, J. B.
    Alexis, J.
    Bardel, D.
    PROCEEDINGS OF THE 9TH INTERNATIONAL SYMPOSIUM ON SUPERALLOY 718 & DERIVATIVES: ENERGY, AEROSPACE, AND INDUSTRIAL APPLICATIONS, 2018, : 805 - 815
  • [50] Slip analysis in a Ni-base superalloy
    Westbrooke, EF
    Forero, LE
    Ebrahimi, F
    ACTA MATERIALIA, 2005, 53 (07) : 2137 - 2147
12345