Fatigue of alumina under contact loading

被引：11
|
作者：
Fett, T [1 ]
Keller, R [1 ]
Munz, D [1 ]
Ernst, E [1 ]
Thun, G [1 ]
机构：
[1] Forschungszentrum Karlsruhe, Inst Materialforsch 2, D-76021 Karlsruhe, Germany
来源：
ENGINEERING FRACTURE MECHANICS | 2003年 / 70卷 / 09期
关键词：
contact loading; cyclic fatigue; multiaxiality; roller loading device;
D O I：
10.1016/S0013-7944(02)00094-2
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Bars cyclically loaded by opposite concentrated forces via rollers are appropriate test specimens for the determination of fatigue under contact loading. As practical applications of the proposed test, the contact strengths and numbers of cycles to failure under contact loading were determined for three Al2O3. In additional tests the residual strength after a pre-loading under contact loading conditions was determined in four-point bending tests. (C) 2002 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：1143 / 1152
页数：10
相关论文
共 50 条
  • [21] Stress intensity factors for subsurface fatigue crack growth under contact loading
    Glodez, S
    Ren, Z
    Flasker, J
    [J]. DAMAGE AND FRACTURE MECHANICS: COMPUTER AIDED ASSESSMENT AND CONTROL, 1998, : 409 - 418
  • [22] Fatigue of railway wheels and rails under rolling contact and thermal loading - an overview
    Ekberg, A
    Kabo, E
    [J]. WEAR, 2005, 258 (7-8) : 1288 - 1300
  • [23] Fatigue behaviour of 42CrMo4 steel under contact loading
    Goencz, Peter
    Potocnik, Rok
    Glodez, Srecko
    [J]. FATIGUE 2010, 2010, 2 (01): : 1991 - 1999
  • [24] Contact fatigue of carburized steels under impact or impact-abrasive loading
    Khrunyk, RA
    [J]. MATERIALS SCIENCE, 2000, 36 (06) : 916 - 921
  • [25] Contact Fatigue of Carburized Steels under Impact or Impact-Abrasive Loading
    R. A. Khrunyk
    [J]. Materials Science, 2000, 36 : 916 - 921
  • [26] OBSERVATION OF FATIGUE DEFORMATION IN CONTACT LOADING
    CHINNERY, M
    [J]. MECHANICAL ENGINEERING, 1967, 89 (08): : 54 - &
  • [27] Hertzian contact fatigue on alumina/alumina-zirconia laminated composites
    Jiménez-Piqué, E
    Ceseracciu, L
    Chalvet, F
    Anglada, M
    de Portu, G
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2005, 25 (15) : 3393 - 3401
  • [28] Contact damage response of alumina-based layered architectures under different loading configurations
    [J]. Bermejo, Raul (raul.bermejo@unileoben.ac.at), 2025, 45 (03)
  • [29] SUBSURFACE FATIGUE FRACTURE IN THE FAST-SPINNING REDUCTOR GEARWHEEL UNDER CONTACT LOADING
    Nikitin, I. S.
    Burago, N. G.
    Nikitin, A. D.
    Stratula, B. A.
    [J]. INTERFACIAL PHENOMENA AND HEAT TRANSFER, 2023, 11 (03) : 61 - 70
  • [30] Eddy Current Testing of Fatigue Degradation of Metastable Austenitic Steel under Gigacycle Contact-Fatigue Loading
    Savrai, R. A.
    Kogan, L. Kh
    [J]. RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 2021, 57 (05) : 393 - 400
12345