Fatigue of alumina under contact loading

被引：11

作者：

Fett, T ^{[1
]}

Keller, R ^{[1
]}

Munz, D ^{[1
]}

Ernst, E ^{[1
]}

Thun, G ^{[1
]}

机构：

[1] Forschungszentrum Karlsruhe, Inst Materialforsch 2, D-76021 Karlsruhe, Germany

来源：

ENGINEERING FRACTURE MECHANICS | 2003年 / 70卷 / 09期

关键词：

contact loading; cyclic fatigue; multiaxiality; roller loading device;

D O I：

10.1016/S0013-7944(02)00094-2

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

Bars cyclically loaded by opposite concentrated forces via rollers are appropriate test specimens for the determination of fatigue under contact loading. As practical applications of the proposed test, the contact strengths and numbers of cycles to failure under contact loading were determined for three Al2O3. In additional tests the residual strength after a pre-loading under contact loading conditions was determined in four-point bending tests. (C) 2002 Elsevier Science Ltd. All rights reserved.

引用

页码：1143 / 1152

页数：10

共 50 条

[1] Fatigue failure of coarse-grained alumina under contact loading
Fett, T
Kraft, O
Munz, D
[J]. MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2005, 36 (3-4) : 163 - 170
[2] Fatigue of Alumina Under Cyclic Torsion Loading
Schwind, Thomas
Kerscher, Eberhard
Lang, Karl-Heinz
[J]. ADVANCED ENGINEERING MATERIALS, 2009, 11 (07) : 586 - 589
[3] Fatigue wear of materials under dynamic contact loading
Bogdanovich, P. N.
[J]. JOURNAL OF FRICTION AND WEAR, 2013, 34 (05) : 349 - 357
[4] Fatigue wear of materials under dynamic contact loading
P. N. Bogdanovich
[J]. Journal of Friction and Wear, 2013, 34 : 349 - 357
[5] Subsurface fatigue crack growth under contact loading
Glodez, S
Ren, Z
Flasker, J
[J]. COMPUTATIONAL PLASTICITY: FUNDAMENTALS AND APPLICATIONS, PTS 1 AND 2, 1997, : 1043 - 1048
[6] On the Effect of Contact Geometry on Fretting Fatigue Life Under Cyclic Contact Loading
G. H. Majzoobi
F. Abbasi
[J]. Tribology Letters, 2017, 65
[7] On the Effect of Contact Geometry on Fretting Fatigue Life Under Cyclic Contact Loading
Majzoobi, G. H.
Abbasi, F.
[J]. TRIBOLOGY LETTERS, 2017, 65 (04)
[8] EFFECT OF CONTACT PRESSURE ON FRETTING FATIGUE BEHAVIOR UNDER CYCLIC CONTACT LOADING
Abbasi, F.
Majzoobi, G. H.
[J]. SURFACE REVIEW AND LETTERS, 2017, 24
[9] EFFECT OF COMPRESSIVE STRESS ON FATIGUE OF ALUMINA UNDER UNIAXIAL CYCLIC LOADING
KIM, KT
SUH, J
[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1993, 76 (01) : 229 - 231
[10] SIMULATION OF FATIGUE CRACK PROPAGATION UNDER CONTACT LOADING CONDITIONS
Jurenka, J.
Spaniel, M.
Kuzelka, J.
[J]. ENGINEERING MECHANICS 2011, 2011, : 255 - 258

← 1 2 3 4 5 →