Improving Electrocatalysts for Oxygen Evolution Using NixFe3-xO4/Ni Hybrid Nanostructures Formed by Solvothermal Synthesis

Spinel-type oxides have been found to be active electrocatalysts for OER. However, their semiconductor character severely limits their catalytic performance. Herein, we report a facile solvothermal pathway for the synthesis of spinel-type NixFe3-xO4 oxides/Ni metal nanocomposites. The good electrical contact between the metal and semiconductor oxide interface and well tuned compositions of NixFe3-xO4 spinel oxides are crucial to achieve better OER performance. Specifically, the NixFe3-xO4/Ni nanocomposite sample prepared from a metal precursor ratio of y = 0.15 [y = Fe/(Fe + Ni)] that results in an x value of about 0.36 exhibits catalytic activity with an overpotential of 225 mV to achieve an electrocatalytic current density of j = 10 mA cm(-2) and a Tafel slope of 44 mV dec(-1) in alkaline electrolyte. This study not only provides new perspectives to designing nanocomposite catalysts for OER but also opens a promising avenue for further enhancing electrocatalytic performance via interface and composition engineering.