EFFECTS OF GRAIN BOUNDARY MORPHOLOGIES ON STRESS CORROSION CRACKING OF ALLOY 600

被引：4
|
作者：
Kim, H. P. [1 ]
Choi, M. J. [1 ]
Kim, S. W. [1 ]
Kim, D. J. [1 ]
Lim, Y. S. [1 ]
Hwang, S. S. [1 ]
机构：
[1] Korea Atom Energy Res Inst, Nucl Mat Safety Res Div, 989-111 Daedeok Daero, Daejeon 305353, South Korea
来源：
ARCHIVES OF METALLURGY AND MATERIALS | 2017年 / 62卷 / 02期
基金：
新加坡国家研究基金会;
关键词：
Alloy; 600; NaOH; stress corrosion cracking; grain boundary morphologies; CREEP-RUPTURE PROPERTIES; INTERGRANULAR CORROSION; SENSITIZATION; MICROSTRUCTURE; INCONEL-600; BEHAVIOR; DESIGN;
D O I：
10.1515/amm-2017-0219
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Effects of grain boundary morphologies on stress corrosion cracking (SCC) of Alloy 600 have been studied in 40% NaOH at 315 degrees C using C-ring specimens. The configuration of the grain boundary and the intergranular carbide density were controlled by heat treatment. SCC tests were performed at + 150 mV above the corrosion potential. The specimen with a serrated grain boundary showed higher SCC resistance than that with a straight grain boundary. This appears to be caused by the fact that the specimen with the serrated grain boundary has longer SCC path. SCC resistance also increased with intergranular carbide density probably due to enhanced relaxation of stress at intergranular carbide.
引用
收藏
页码：1415 / 1419
页数：5
相关论文
共 50 条
  • [41] DIRECTIONAL EFFECTS IN STRESS CORROSION CRACKING OF AN ALUMINUM ALLOY
    UGIANSKY, GM
    SKOLNICK, LP
    STIEFEL, SW
    CORROSION, 1969, 25 (02) : 77 - &
  • [42] On the heat treatment and microstructure in the intergranular stress corrosion cracking response of alloy 600
    Aguilar, A
    Albarrán, JL
    López, HF
    Martínez, L
    HYDROGEN EFFECTS ON MATERIAL BEHAVIOR AND CORROSION DEFORMATION INTERACTIONS, 2003, : 733 - 740
  • [43] Dielectrostriction and Intergranular Stress Corrosion Cracking of Alloy 600 in PWR Primary Water
    Devine, Thomas M.
    CORROSION, PASSIVITY, AND ENERGY: A SYMPOSIUM IN HONOR OF DIGBY D. MACDONALD, 2013, 50 (31): : 91 - 97
  • [44] General corrosion and stress corrosion cracking of Alloy 600 in light water reactor primary coolants
    Scott, Peter M.
    Combrade, Pierre
    JOURNAL OF NUCLEAR MATERIALS, 2019, 524 : 340 - 375
  • [45] RELATIONSHIP BETWEEN ACID INTERGRANULAR CORROSION AND CAUSTIC STRESS-CORROSION CRACKING OF ALLOY 600
    THEUS, GJ
    CORROSION, 1977, 33 (01) : 20 - 26
  • [46] Decarburization, grain boundary segregation of P and primary water stress corrosion cracking in a low-alloy steel
    Heo, N. H.
    Jung, Y. C.
    Lee, J. K.
    Kim, K. T.
    SCRIPTA MATERIALIA, 2008, 59 (11) : 1200 - 1203
  • [47] Correlations between stress corrosion cracking susceptibility and grain boundary microstructures for an Al-Zn-Mg alloy
    Sun, X. Y.
    Zhang, B.
    Lin, H. Q.
    Zhou, Y.
    Sun, L.
    Wang, J. Q.
    Han, E. -H.
    Ke, W.
    CORROSION SCIENCE, 2013, 77 : 103 - 112
  • [48] Stress corrosion cracking of alloy 600 and alloy 690 in hydrogen/steam at 380 degrees C
    Sui, G
    Titchmarsh, JM
    Heys, GB
    Congleton, J
    CORROSION SCIENCE, 1997, 39 (03) : 565 - 587
  • [49] Grain boundary engineering for improving stress corrosion cracking of 304 stainless steel
    Liu, Tingguang
    Bai, Qin
    Ru, Xiangkun
    Xia, Shuang
    Zhong, Xiangyu
    Lua, Yonghao
    Shoji, Tetsuo
    MATERIALS SCIENCE AND TECHNOLOGY, 2019, 35 (04) : 477 - 487
  • [50] Grain-boundary modelling of hydrogen assisted intergranular stress corrosion cracking
    Benedetti, Ivano
    Gulizzi, Vincenzo
    Milazzo, Alberto
    MECHANICS OF MATERIALS, 2018, 117 : 137 - 151
12345