Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water

被引：59
|
作者：
Dong, Lijin [1 ,2 ]
Peng, Qunjia [1 ]
Han, En-Hou [1 ]
Ke, Wei [1 ]
Wang, Lei [2 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China
[2] Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China
来源：
CORROSION SCIENCE | 2016年 / 107卷
基金：
中国国家自然科学基金;
关键词：
Stainless steel; SEM; TEM; Stress corrosion; Welding; HIGH-TEMPERATURE WATER; PWR PRIMARY WATER; LOW-ALLOY STEEL; GROWTH; MICROSTRUCTURE; ENVIRONMENT; CHEMISTRY; REGION; 690TT;
D O I：
10.1016/j.corsci.2016.02.030
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Stress corrosion cracking (SCC) in the heat affected zone (HAZ) of a stainless steel 308L-316L weld joint in primary water of pressurized water reactor was investigated. Stress corrosion crack growth in the HAZ was observed in off-normal primary water chemistry with dissolved oxygen, but not in normal primary water chemistry with dissolved hydrogen. This suggests that it is unlikely a stress corrosion crack propagating in the HAZ could reach the fusion boundary and penetrate into the weld metal under normal primary water chemistry conditions. Microstructure analysis of the crack tip suggests that the SCC follows the slip-oxidation mechanism. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：172 / 181
页数：10
相关论文
共 50 条
  • [21] Oxidation Resistance and Stress Corrosion Cracking Susceptibility of 308L and 309L Stainless Steel Cladding Layers in Simulated Pressurized Water Reactor Primary Water
    Cui, Tongming
    Xiong, Qi
    Ma, Jiarong
    Zhang, Kun
    Lu, Zhanpeng
    Chen, Junjie
    Jia, Yibo
    Zheng, Hui
    Yang, Shuangliang
    Zhong, Zhimin
    Lozano-Perez, Sergio
    Shoji, Tetsuo
    CORROSION, 2021, 77 (08) : 878 - 895
  • [22] Evaluation of stress corrosion cracking susceptibility of forged 316 stainless steel in simulated primary water
    Zhu, Ruolin
    Wang, Jianqiu
    Ming, Hongliang
    Zhang, Zhiming
    Han, En-Hou
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2018, 69 (03): : 328 - 336
  • [23] Experimental Study on Chloride Stress Corrosion Cracking Sensitivity of 316L Stainless Steel
    Chen, Fei
    JOURNAL OF ENGINEERING, 2021, 2021
  • [24] Stress corrosion cracking in 316L stainless steel bellows of a pressure safety valve
    Panda, Bijayani
    Sujata, M.
    Madan, M.
    Bhaumik, S. K.
    ENGINEERING FAILURE ANALYSIS, 2014, 36 : 379 - 389
  • [25] Impact of surface condition on sulphide stress corrosion cracking of 316L stainless steel
    Hinds, G.
    Wickstroem, L.
    Mingard, K.
    Turnbull, A.
    CORROSION SCIENCE, 2013, 71 : 43 - 52
  • [26] Effect of laser mode on microstructure and corrosion resistance of 316L stainless steel weld joint
    Yan, Shenghong
    Shi, Yan
    Liu, Jia
    Ni, Cong
    OPTICS AND LASER TECHNOLOGY, 2019, 113 : 428 - 436
  • [27] Microstructure and intergranular stress corrosion cracking susceptibility of a SA508-52M-316L dissimilar metal weld joint in primary water
    Lijin Dong
    Qunjia Peng
    En-Hou Han
    Wei Ke
    Lei Wang
    Journal of Materials Science & Technology, 2018, 34 (08) : 1281 - 1292
  • [28] Stress corrosion cracking on irradiated 316 stainless steel
    Furutani, G
    Nakajima, N
    Konishi, T
    Kodama, M
    JOURNAL OF NUCLEAR MATERIALS, 2001, 288 (2-3) : 179 - 186
  • [29] Microstructure and intergranular stress corrosion cracking susceptibility of a SA508-52M-316L dissimilar metal weld joint in primary water
    Dong, Lijin
    Peng, Qunjia
    Han, En-Hou
    Ke, Wei
    Wang, Lei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (08) : 1281 - 1292
  • [30] Effects of Corrosion Potential, Dissolved Oxygen, and Chloride on the Stress Corrosion Cracking Susceptibility of a 316NG Stainless Steel Weld Joint
    Wang, Jiamei
    Su, Haozhan
    Ajmand, Farzin
    Zhang, Lefu
    Chen, Kai
    CORROSION, 2019, 75 (08) : 946 - 959
12345