Ultrafast laser direct writing on PVP/FTO/Glass substrates to fabricate Ag mesh transparent conductive films

Ag mesh transparent conductive films (TCFs) were prepared on the commercial FTO/Glass substrate by ultrafast laser direct writing, trying to improve its overall photoelectric performances. The effects of laser scanning speed, laser fluence and Ag mesh height on photoelectric properties of the Ag mesh/FTO TCFs were systematically studied. The results indicated that a small scanning speed or a high laser fluence would cause excessive ablation of the FTO film and result in an increased Ag mesh line width, which was detrimental to the photoelectric properties of the resulting TCF. It was found that the optimal parameters for fabricating Ag mesh/FTO TCFs were a laser scanning speed of 2200 mm/s, a laser fluence of 0.050 J/cm(2) and an Ag mesh height of 2500 nm. The asfabricated TCF possessed the highest figure of merit of 13.03 x 10(-2) Omega(-1), which was significantly superior to that of the commercial FTO film. Finally, transparent heaters (THs) were prepared respectively based on the optimal Ag mesh/FTO TCF and the FTO/Glass substrate. The Ag mesh/FTO TH exhibited a more excellent heating performance than the FTO TH, further confirming that the overall photoelectric performance of the FTO/Glass substrate had been greatly improved.