In-situ TEM investigation of failure processes in metal-plastic joint interfaces

被引：5

作者：

Horiuchi, Shin ^{[1
]}

Liu, Yida ^{[1
]}

Shigemoto, Yuri ^{[1
]}

Hanada, Takeshi ^{[1
]}

Shimamoto, Kazumasa ^{[1
]}

机构：

[1] Natl Inst Adv Ind Sci & Technol, Res Lab ForAdhes & Interfacial Phenomena AIRL, 1-1-1 Higashi, Tsukuba, Ibaraki 3058565, Japan

来源：

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES | 2022年 / 117卷

关键词：

Behavior of joint - Cracks propagation - Failure behaviors - Failure process - In-situ straining - In-situ transmission - Joint interfaces - Nano scale - Straining techniques - Transmission electron;

D O I：

10.1016/j.ijadhadh.2021.103003

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

The nano-scale failure behaviors of joint interfaces were investigated by in-situ straining technique to observe the crack propagations in a transmission electron microscope (TEM). The thin sections of bonded interfaces were subjected to tensile loading by using a specially designed specimen holder. The deformation at the crack tip before the initiation of crack and the initiation of the crack were observed in the nanometer level. The experiments with identical and dissimilar polymer/polymer welded specimens allowed us to see the plastic deformation ahead of the crack tip and the creation of craze, which is the typical failure mode of polymers. The failure of the interfaces between aluminum alloy (Al5052) and epoxy adhesive and between Al5052 and thermoplastic directly bonded by injection molding were investigated to visualize the failure behaviors in small scale before the macroscopic fracture of the interfaces. The in-situ straining technique under a high-resolution scanning transmission electron microscopy (STEM) mode enables the observation of micro deformation ahead of the crack, microvoids produced prior to the crack progression and the failure of the surface modified layer on Al surface.

引用

页数：7

共 50 条

[11] In-situ TEM Investigation of Solid Phase Transformations and Reactions
Hajagos-Nagy, Klara
PERIODICA POLYTECHNICA-MECHANICAL ENGINEERING, 2021, 65 (03): : 252 - 260
[12] An in-situ TEM investigation of He bubble evolution in SiC
Pawley, C. J.
Beaufort, M. F.
Oliviero, E.
Hinks, J. A.
Barbot, J. F.
Donnelly, S. E.
ELECTRON MICROSCOPY AND ANALYSIS GROUP CONFERENCE 2011 (EMAG 2011), 2012, 371
[13] In-situ TEM investigation of toughening in Silicon at small scales
Issa, Inas
Gammer, Christoph
Kolitsch, Stefan
Hohenwarter, Anton
Imrich, Peter J.
Pippan, Reinhard
Kiener, Daniel
MATERIALS TODAY, 2021, 48 : 29 - 37
[14] In-situ liquid phase TEM observations of nucleation and growth processes
De Yoreo, James J.
PROGRESS IN CRYSTAL GROWTH AND CHARACTERIZATION OF MATERIALS, 2016, 62 (02) : 69 - 88
[15] Investigation on Switching Operation in Resistive RAM Using In-Situ TEM
Arita, Masashi
Takahashi, Yasuo
3RD INTERNATIONAL MULTIDISCIPLINARY MICROSCOPY AND MICROANALYSIS CONGRESS (INTERM), 2017, 186 : 205 - 214
[16] In-Situ TEM Investigation of Deformation Behavior of Metallic Glass Pillars
Chen, C. Q.
Pei, Y. T.
De Hosson, J. Th. M.
PROBING MECHANICS AT NANOSCALE DIMENSIONS, 2009, 1185 : 99 - 104
[17] Behaviour of TEM metal grids during in-situ heating experiments
Zhang, Zaoli
Su, Dangsheng
ULTRAMICROSCOPY, 2009, 109 (06) : 766 - 774
[18] In-situ TEM imaging of the anisotropic etching of graphene by metal nanoparticles
Wei, Jiake
Xu, Zhi
Wang, Hao
Tian, Xuezeng
Yang, Shize
Wang, Lifen
Wang, Wenlong
Bai, Xuedong
NANOTECHNOLOGY, 2014, 25 (46)
[19] In-situ TEM observation of internal metal inside metal filled carbon fiber
Tokunaga, Tomoharu
Horita, Yoshiro
Kanematsu, Takumi
Nomura, Ikuo
Iijima, Toru
Hayashi, Yasuhiko
Kuroda, Kotaro
DIAMOND AND RELATED MATERIALS, 2011, 20 (02) : 210 - 212
[20] In-situ SEM and TEM continuous observations for studying dynamic processes in materials
Lei, TQ
MATERIALS AND MANUFACTURING PROCESSES, 1997, 12 (01) : 61 - 69

← 1 2 3 4 5 →