Ion implanted AZ31 magnesium alloy

被引：9
|
作者：
Wu, Guosong [1 ]
Zeng, Xiaoqin [1 ]
Yao, Shoushan [1 ]
Han, Haibo [2 ]
机构：
[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Shanghai 200030, Peoples R China
[2] Shanghai Jiao Tong Univ, Inst Anal Ctr, Shanghai 200030, Peoples R China
来源：
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM | 2007年 / 546-549卷
关键词：
AZ31 Mg alloy; ion implantation; surface morphology; corrosion property;
D O I：
10.4028/www.scientific.net/MSF.546-549.551
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Ion implantation was applied to modify the surface properties of magnesium alloy. About 75 keV titanium ions with a dose of 5x10(17) ions/cm(-2) and about 35 keV nitrogen ions with a dose of 3x10(17) ions/cm(-2) were implanted into AZ31 magnesium alloy, respectively. AFM and FESEM were used to examine the surface morphology of the treated samples. In contrast to the smooth surface treated by N ion implantation, the Ti-treated surface was severely damaged. AES analysis reveals that both kinds of ions implanted in AZ31 magnesium alloy took on a quasi-Gaussian distribution in the near surface region. In the corrosion test, the N-implanted sample showed a better corrosion resistance in 3.5wt.% NaCl solution than bare AZ31 sample, whereas the Ti-implanted sample accelerated the corrosion behavior of AZ31 in this solution.
引用
收藏
页码：551 / +
页数：2
相关论文
共 50 条
  • [11] Evaluation on the formability of magnesium alloy, AZ31
    Yong, MS
    Hu, BH
    Choy, CM
    Kreij, AV
    ADVANCED MATERIALS PROCESSING II, 2003, 437-4 : 435 - 438
  • [12] The press formability in magnesium alloy AZ31
    Somekawa, H
    Kohzu, M
    Tanabe, S
    Higashi, K
    MAGNESIUM ALLOYS 2000, 2000, 350-3 : 177 - 182
  • [13] Shear bands in magnesium alloy AZ31
    Yang, P
    Mao, WM
    Ren, XP
    Tang, QB
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2004, 14 (05) : 851 - 857
  • [14] Anticorrosive magnesium phosphate coating on AZ31 magnesium alloy
    Ishizaki, Takahiro
    Shigematsu, Ichinori
    Saito, Naobumi
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (16): : 2288 - 2291
  • [15] The effect of Y-ion implantation on the oxidation of AZ31 magnesium alloy
    Wang, Xuemin
    Zeng, Xiaoqin
    Wu, Guosong
    Yao, Shoushan
    MATERIALS LETTERS, 2007, 61 (4-5) : 968 - 970
  • [16] Formability and microstructure of AZ31 magnesium alloy sheets
    Forcellese, A.
    El Mehtedi, M.
    Simoncini, M.
    Spigarelli, S.
    SHEET METAL 2007, 2007, 344 : 31 - +
  • [17] Developing superplasticity in a magnesium AZ31 alloy by ECAP
    Roberto B. Figueiredo
    Terence G. Langdon
    Journal of Materials Science, 2008, 43 : 7366 - 7371
  • [18] Tensile behaviors of fatigued AZ31 magnesium alloy
    Shu, Yang
    Zhang, Xi-yan
    Yu, Jiang-ping
    Tan, Li
    Yin, Rui-sen
    Liu, Qing
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2018, 28 (05) : 896 - 901
  • [19] Constitutive analysis of AZ31 magnesium alloy plate
    Yu Kun
    Cai Zhi-yong
    Wang Xiao-yan
    Shi Ti
    Li Wen-xian
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2010, 17 (01): : 7 - 12
  • [20] Warm hydroforming of magnesium alloy AZ31 sheets
    Zhang, S. H.
    Ren, L. M.
    Zhou, L. X.
    Xu, Y. C.
    Palumbo, G.
    Ricarico, L. T.
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 333 - +
12345