Corrosion cracking of welded joints of pipelines from steel 08Kh18N10T in power units with RBMK-type reactors

被引：0

作者：

Zubchenko, A. S. ^{[1
]}

Kharina, I. L. ^{[1
]}

Runov, A. E. ^{[1
]}

Mukhin, A. V. ^{[1
]}

Korovin, N. Yu. ^{[1
]}

机构：

[1] NPO TsNIITMASh Co, Moscow, Russia

来源：

METAL SCIENCE AND HEAT TREATMENT | 2007年 / 49卷 / 1-2期

关键词：

Welds;

D O I：

10.1007/s11041-007-0016-7

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The effect of coolant parameters (temperature, content of oxygen and chlorine ions, acidity parameter pH) and of residual stresses on the susceptibility of welded joints of pipelines from steel 08Kh18N10T at power units with RBMK-type reactors to intercrystalline corrosion cracking is studied. It is shown that the endurance of the pipelines depends on the heat treatment of welded joints and on the deaerated rise of the reactor to the operating conditions.

引用

页码：82 / 88

页数：7

共 50 条

[21] STRAINS IN, AND THE NATURE OF FAILURE OF, BRAZED JOINTS IN THE 08KH18N10T STEEL IN STRUCTURES OF THERMAL POWER-PLANT
ORLOV, AV
WELDING PRODUCTION, 1981, 28 (04): : 35 - 37
[22] High temperature hot ductility of the 08Kh18N10T steel and its electroslag welded joint
Astaf'ev, A.A.
Lepekhina, L.I.
Batieva, N.M.
Viktorov, N.A.
Tyazheloe Mashinostroenie, 1992, (12): : 30 - 33
[23] CORROSION RESISTANCE OF STRAINED WELDED JOINTS IN STEEL KH18N10T
MIGAI, LL
VEDENEEV.MA
ZHUK, NP
WELDING PRODUCTION, 1969, 16 (04): : 78 - &
[24] CORROSION-RESISTANCE OF BRAZED JOINTS IN STEELS 20 AND 08KH18N10T USED IN THERMAL POWER-PLANTS
ORLOV, AV
WELDING PRODUCTION, 1978, 25 (02): : 38 - 40
[25] SURFACE-STATE, STRESS-CORROSION CRACKING, AND PITTING CORROSION OF STEEL 08KH18N10T IN MGCL2 SOLUTION
LEVCHENKO, VA
KUZYUKOV, AN
NIKHAENKO, YY
NOVITSKII, VS
PROTECTION OF METALS, 1986, 22 (01): : 94 - 96
[26] INFLUENCE OF STRUCTURE ON THE TENDENCY OF 08KH18N10T STAINLESS-STEEL TOWARD INTERGRANULAR CORROSION
GOLDSHTEIN, VY
ZAVYALOVA, VI
PISKUNOVA, AI
METAL SCIENCE AND HEAT TREATMENT, 1981, 23 (5-6) : 446 - 450
[27] Influence of the Parameters of Feed Water of the WWER-1000 Reactors on the Corrosion-Electrochemical Behavior of 08KH18N10T Steel
Pokhmurs'kyi, V. I.
Khoma, M. S.
Antoshchak, I. M.
Vorobel', V. I.
MATERIALS SCIENCE, 2015, 50 (06) : 897 - 902
[28] INFLUENCE OF STRUCTURE ON THE TENDENCY OF 08Kh18N10T STAINLESS STEEL TOWARD INTERGRANULAR CORROSION.
Gol'dshtein, V.Ya.
Zav'yalova, V.I.
Piskunova, A.I.
1600, (23): : 5 - 6
[29] Influence of the Parameters of Feed Water of the WWER-1000 Reactors on the Corrosion-Electrochemical Behavior of 08KH18N10T Steel
V. І. Pokhmurs’kyi
М. S. Khoma
І. М. Antoshchak
V. І. Vorobel
Materials Science, 2015, 50 : 897 - 902
[30] MANUFACTURING TECHNOLOGY CENTRIFUGAL ELECTROSLAG CASTING FOR 08Kh18N10T STEEL
Zherebtsov, S. N.
Fat'yanov, S. V.
CHEMICAL AND PETROLEUM ENGINEERING, 2006, 42 (1-2) : 114 - 116

← 1 2 3 4 5 →