Experimental Determination and Thermodynamic Modeling of the Sn-Rich Corner of the Ternary Ni-Pd-Sn Phase Diagram at 250°C

被引:7
|
作者
Rahman, Md. Arifur [1 ]
Ho, Cheng En [1 ]
Gierlotka, Wojciech [2 ]
Kuo, Jui Chao [3 ]
机构
[1] Yuan Ze Univ, Dept Chem Engn & Mat Sci, Chungli 320, Taoyuan, Taiwan
[2] Natl Dong Hwa Univ, Dept Mat Sci & Engn, Shoufeng 97401, Hualien, Taiwan
[3] Natl Cheng Kung Univ, Dept Mat Sci & Engn, Tainan 701, Taiwan
关键词
Ni-Pd-Sn isotherm; Muggianu method; CALPHAD; EBSD; SOLDER JOINTS; MICROSTRUCTURAL EVOLUTION; ALLOYS; TIN; SN-3AG-0.5CU; THICKNESS; AG;
D O I
10.1007/s11664-014-3330-z
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
The Sn-rich portion of the phase diagram for the Ni-Pd-Sn ternary system was preliminarily obtained by interpolation of the three constituent binary systems using the Muggianu method. Based on this proposition, 23 Ni-Pd-Sn alloys were prepared and annealed at 250 degrees C. The annealed alloys were analyzed by scanning electron microscopy, electron probe microanalysis, electron backscatter diffraction, and x-ray diffraction. All the binaries adjacent to the Sn-rich corner (i.e., PdSn4, PdSn3, PdSn2, and Ni3Sn4) were found to have remarkable ternary solubility. The experimental results presented herein, together with a thermodynamic interpolation of the ternary system based on the results from the binary systems, were used to calculate the ternary phase diagram using the calculation of phase diagrams (CALPHAD) method. A substitution model was used to describe the Gibbs free energies of the liquid and solid solution phases, and a sublattice model was used to describe intermetallic compounds. A consistent set of thermodynamic parameters was obtained, ultimately leading to a better fit between the calculated results and the experimental data for this system.
引用
收藏
页码:4582 / 4593
页数:12
相关论文
共 50 条
  • [21] Wetting transition of grain boundaries in the Sn-rich part of the Sn–Bi phase diagram
    C.-H. Yeh
    L.-S. Chang
    B. B. Straumal
    Journal of Materials Science, 2011, 46 : 1557 - 1562
  • [22] Wetting transition of grain boundaries in the Sn-rich part of the Sn-Bi phase diagram
    Yeh, C. -H.
    Chang, L. -S.
    Straumal, B. B.
    JOURNAL OF MATERIALS SCIENCE, 2011, 46 (05) : 1557 - 1562
  • [23] Phase Equilibria of the Sn-Ni-V System: The 980A°C Isothermal Section and the Sn-Rich Corner at 600A°C and 300A°C
    Wu, Changjun
    Su, Xuping
    Peng, Haoping
    Liu, Ya
    Tu, Hao
    Wang, Jianhua
    JOURNAL OF ELECTRONIC MATERIALS, 2015, 44 (10) : 3904 - 3913
  • [24] Phase equilibria in Sn rich corner of Cu-Ni-Sn system
    Snugovsky, L.
    Snugovsky, P.
    Perovic, D. D.
    Rutter, J. W.
    MATERIALS SCIENCE AND TECHNOLOGY, 2006, 22 (08) : 899 - 902
  • [25] Thermodynamic analysis of the Sn-In-Sb ternary phase diagram
    Ishihara, S
    Ohtani, H
    Saito, T
    Ishida, K
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1999, 63 (06) : 695 - 701
  • [26] Thermodynamic analysis of the Sn-In-Sb ternary phase diagram
    Toyota Ctrl. R. and D. Labs., Inc., Aichi-gun 480-1192, Japan
    不详
    不详
    不详
    Nippon Kinzoku Gakkaishi, 6 (695-701):
  • [27] Isothermal section of ternary Sn-Zn-Ni phase equilibria at 250 °C
    Chen, Sinn-wen
    Hsu, Chia-ming
    Chou, Chin-yi
    Hsu, Che-wei
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2011, 21 (05) : 386 - 391
  • [28] Thermodynamic analysis of the Sn-Ag-Bi ternary phase diagram
    Ohtani, H
    Satoh, I
    Miyashita, M
    Ishida, K
    MATERIALS TRANSACTIONS, 2001, 42 (05) : 722 - 731
  • [29] Experimental phase diagram of the ternary Bi-Sn-Zn
    Braga, M. H.
    Malheiros, L. F.
    Soares, D.
    Ferreira, J.
    Castro, F.
    ADVANCED MATERIALS FORUM III, PTS 1 AND 2, 2006, 514-516 : 1682 - 1686
  • [30] Experimental Phase Diagram of the Ag-Se-Sn System at 250, 400 and 550 °C
    Ondrej Zobac
    Klaus W. Richter
    Ales Kroupa
    Journal of Phase Equilibria and Diffusion, 2022, 43 : 32 - 42