Preparation and properties of ZnMoO4 anode materials with polymer network gel method

Polymer network gel method combines the advantages of solid-phase method and liquid phase method, triggering acrylamide (AM) radical polymerization in aqueous solution and N, N '- methylene bis acrylamide (MBAM) active double bond cross-linking reaction, forming polymer chains to form a three-dimensional network. The polymer network space formed by the gel is bound and evenly distributed to the ions in the solution, thereby reducing the contact and aggregation of molecules and achieving the purpose of uniform particle size and small particle size. The principle diagram of network gel is shown in Figure. Using cubic zinc acetate and ammonium molybdate tetrahydrate as raw materials, cubic ZnMoO4 negative electrode materials were prepared with polymer network gel method. The polymer network gel method has various effects on the structure, morphology and electrochemical properties of materials. Besides, the calcination temperature and calcination time were also the key factors to the electrochemical properties of the materials. In this paper, the effects of the ratio of monomer and crosslinker, calcination temperature and calcination time on ZnMoO4 materials were studied by single variable method, the preparation process was optimized, and its characterization and electrochemical tests were carried out. After 100 cycles, the optimized ZnMoO4 electrode has a discharge capacity of 374.0 mAh. g(-1), 332.5, 263.5 and 177.1 mAh.g(-1) at current densities of 0.1, 0.5, 1.0 and 2.0 A g(-1), respectively. The electrochemical results show that the optimized ZnMoO4 has high capacity, large rate capability and excellent cycle stability.