Effect of Ti content in Ag-Cu-Ti activated filler metal on dissimilar joint formation of sialon and WC-Co alloy by laser brazing

被引：6

作者：

Nagatsuka, K. ^{[1
]}

Yoshida, S. ^{[1
]}

Sechi, Y. ^{[1
]}

Nakata, K. ^{[1
]}

机构：

[1] Osaka Univ, Joining & Welding Res Inst, Ibaraki, Osaka 5670047, Japan

来源：

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2014年 / 19卷 / 06期

关键词：

Laser brazing; Sialon; WC-Co alloy; Ag-Cu-Ti filler metal; Interface structure; BRAZED JOINTS; MICROSTRUCTURE; STRENGTH; CERAMICS; NITRIDE; STEEL; SI3N4;

D O I：

10.1179/1362171814Y.0000000217

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Laser brazing was carried out for dissimilar joining of sialon and a WC-Co alloy. Eutectic type Ag-Cu alloys as filler metals with different Ti content ranging from 0 to 2.8 mass-% were used to investigate the effects of Ti on the interface structure and strength of the joint. The filler metal sheet was sandwiched between a sialon block and a WC-Co alloy plate, and a laser beam was irradiated selectively on the WC-Co alloy plate. The brazed joint was obtained using the filler metal containing.0.3 mass-% Ti. TiN, Ti5Si3, and Cu4Ti layers were formed at the interface of sialon and brazed metal as compound layers. The shear strength of the brazed joint increased with increasing Ti content in the filler metal in the range 0.3-1.7 mass-%, reaching a maximum value of 106 MPa. However, the strength decreased when the Ti content became higher than 1? 7 mass-%.

引用

页码：521 / 526

页数：6

共 50 条

[41] Microstructure and properties of WC-Co cemented carbide/40Cr steel joints brazed at low-temperature with Ag-Cu-In-Ti filler alloy
Zheng, Zhaoyang
Shao, Shuai
Xu, Minyun
Ma, Ruina
Du, An
Fan, Yongzhe
Zhao, Xue
Cao, Xiaoming
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2023, 111
[42] FORMATION OF INTERFACIAL MICROSTRUCTURE IN BRAZING OF SI3N4 WITH TI-ACTIVATED AG-CU FILLER ALLOYS
PAULASTO, M
KIVILAHTI, JK
SCRIPTA METALLURGICA ET MATERIALIA, 1995, 32 (08): : 1209 - 1214
[43] Effect of processing parameters on the formation of Cf/LAS composites/Ag-Cu-Ti/TC4 brazed joint
Liu, Duo
Niu, Hongwei
Liu, Jihou
Song, Xiaoguo
Xia, Long
Feng, Jicai
MATERIALS CHARACTERIZATION, 2016, 120 : 249 - 256
[44] Vacuum brazing of TiAl-based intermetallics with Ti-Zr-Cu-Ni-Co amorphous alloy as filler metal
Li, Xiaoqiang
Li, Li
Hu, Ke
Qu, Shengguan
INTERMETALLICS, 2015, 57 : 7 - 16
[45] Interfacial microstructure and mechanical property of SiO2-BN ceramics and Invar joint brazed with Ag-Cu-Ti active filler metal
Yang, Z. W.
Zhang, L. X.
Xue, Q.
He, P.
Feng, J. C.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 534 : 309 - 313
[46] Effect of Si3N4-particles addition in Ag-Cu-Ti filler alloy on Si3N4/TiAl brazed joint
Song, X. G.
Cao, J.
Wang, Y. F.
Feng, J. C.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (15): : 5135 - 5140
[47] Microstructure and mechanical properties of Al2O3 ceramic and TiAl alloy joints brazed with Ag-Cu-Ti filler metal
Niu, G. B.
Wang, D. P.
Yang, Z. W.
Wang, Y.
CERAMICS INTERNATIONAL, 2016, 42 (06) : 6924 - 6934
[48] Vacuum brazing of Cf/β-spodumene composites and Ti-6Al-4 V alloy using Ag-Cu filler metal
Song, X. G.
Zhao, Y. X.
Niu, H. W.
Liu, J. H.
Liu, D.
Xia, L.
Bian, H.
Feng, J. C.
MATERIALS CHARACTERIZATION, 2017, 132 : 354 - 362
[49] Effect of brazing temperature and holding time on joint properties of induction brazed WC-Co/carbon steel using Ag-based alloy
Jiang, Chao
Chen, Hui
Wang, Qiuying
Li, Yuanxing
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2016, 229 : 562 - 569
[50] Releasing the residual stress of Al2O3/304 stainless steel joint by introducing BN into Ag-Cu-Ti filler metal
Li, Tao
Xue, Haitao
Meng, Xianming
Guo, Weibing
Zhang, Sai
Wu, Hao
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2024, 21 (03) : 2235 - 2245

← 1 2 3 4 5 →