A super-microporous zirconia-alumina nanomaterial with high thermal stability

被引：7
|
作者：
Li, Yongfeng [1 ]
Su, JiaoJiao [1 ]
Ma, Jinghong [1 ]
Yu, Feng [1 ]
Pan, Dahai [1 ]
Li, Ruifeng [1 ]
机构：
[1] Taiyuan Univ Technol, Coll Chem & Chem Engn, Taiyuan 030024, Peoples R China
来源：
MATERIALS LETTERS | 2014年 / 136卷
基金：
山西省青年科学基金; 中国国家自然科学基金;
关键词：
Super-microporous zirconia-alumina; Large surface area; Thermal stability; MESOPOROUS ALUMINA; FACILE SYNTHESIS; CATALYSTS;
D O I：
10.1016/j.matlet.2014.08.004
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A super-microporous zirconia-alumina (pore size in the range of 1-2 nm) with narrow pore size distribution has been synthesized successfully by using an inexpensive nonionic surfactant fatty alcohol polyoxyethylene ether (AEO-7) as the template in ethanol solvent. As the Zr/Al molar ratio is 0.1, the material has high surface area of 413 m(2)/g and a large pore volume of 0.17 cm(3)/g after calcination at 400 degrees C. Even after calcination at 900 degrees C, the microporous structure remained, exhibiting a significant thermal stability. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码：183 / 186
页数：4
相关论文
共 50 条
  • [21] High resolution electron microscopy of sputter-deposited zirconia-alumina nanolaminates
    Schofield, MA
    Whig, R
    Aita, CR
    GajdardziskaJosifovska, M
    POLYCRYSTALLINE THIN FILMS: STRUCTURE, TEXTURE, PROPERTIES, AND APPLICATIONS II, 1996, 403 : 297 - 301
  • [22] Improvement of thermal stability of alumina by addition of zirconia
    Horiuchi, T
    Teshima, Y
    Osaki, T
    Sugiyama, T
    Suzuki, K
    Mori, T
    CATALYSIS LETTERS, 1999, 62 (2-4) : 107 - 111
  • [23] Improvement of thermal stability of alumina by addition of zirconia
    Tatsuro Horiuchi
    Yutaka Teshima
    Toshihiko Osaki
    Toyohiko Sugiyama
    Kenzi Suzuki
    Toshiaki Mori
    Catalysis Letters, 1999, 62 : 107 - 111
  • [24] Yttria-stabilized zirconia-alumina composite sintering temperature effect on thermal diffusivity
    Dychton, Kamil
    Drajewicz, Marcin
    Pytel, Maciej
    Rokicki, Pawe
    Nowotnik, Andrzej
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2016, 126 (01) : 1 - 7
  • [25] Influence of abrasive machining and annealing on hydrothermal stability of zirconia-alumina composites as a hip joint head
    Lim, H. -B.
    Oh, K. -S.
    Kwon, Y. -J.
    Kim, Y-K.
    Lee, D. Y.
    BIOCERAMICS, VOL 19, PTS 1 AND 2, 2007, 330-332 : 1223 - +
  • [26] Microstructural stability of zirconia-alumina composite coatings during hot corrosion test at 1050°C
    Keyvani, A.
    Saremi, M.
    Sohi, M. Heydarzadeh
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 506 (01) : 103 - 108
  • [27] One-pot synthesis of a new high-aluminium-content super-microporous aluminosilicate
    Huerta, Lenin
    Romero-Sarria, Francisca
    Marie, Olivier
    Guillem, Carmen
    Beltran, Aurelio
    Latorre, Julio
    Beltran, Daniel
    Amoros, Pedro
    EUROPEAN JOURNAL OF INORGANIC CHEMISTRY, 2006, (16) : 3147 - 3151
  • [28] Study on thermal shock resistance of zirconia-alumina refractory prepared by wet-chemical process
    Xu, Lihua
    Lian, Fang
    Li, Wenchao
    Nie, Guiqiu
    He, Rusheng
    Bai, Jizhou
    Ferreira, Jose Maria Fonte
    2000, Luoyang Naihuo Cailiao Yanjiusuo, China (34):
  • [29] Fracture behavior and thermal shock resistance of alumina-spinel castables-Effect of added fused zirconia-alumina
    Yu, Renhong
    Zhang, Liyuan
    Zhang, Xiaohui
    Liu, Pengcheng
    Qi, Haoyuan
    Wang, Junhao
    Liu, Xinhong
    CERAMICS INTERNATIONAL, 2020, 46 (13) : 20732 - 20741
  • [30] THERMAL-STABILITY AND PORE SIZES OF MICROPOROUS ZIRCONIA GELS
    RAHMAN, AA
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1983, 1 (02): : 263 - 266
12345