Fabrication of Indium Tin Oxide targets by Spark Plasma Sintering and Hot-Pressing Sintering

被引：3
|
作者：
Guo, Wei [1 ]
Wang, Weimin [1 ]
Wang, Hao [1 ]
Wang, Yucheng [1 ]
Fu, Zhengyi [1 ]
机构：
[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China
来源：
ADVANCED SYNTHESIS AND PROCESSING TECHNOLOGY FOR MATERIALS | 2009年 / 66卷
关键词：
Fabrication; Sintering; densification; ITO; SnO2; ITO;
D O I：
10.4028/www.scientific.net/AMR.66.96
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The Indium Tin Oxide(ITO) is known as a poorly sinterable material The Spark Plasma Sintering(SPS) and the hot-pressing sintering(HP) were used to fabricate Indium Tin Oxide Ceramics from ITO nanoparticles. The maximum bulk density of 7 02 g/cm(2)(relative density; 98.2% TD)was obtained when sintered in Ar at 1000 degrees C for lmin by SPS sintering While the bulk density of 7 08 g/cm(2)(relative density, 99% TD) was obtained when sintered in Ar at 1050 degrees C for 4h by HP sintering
引用
收藏
页码：96 / 99
页数：4
相关论文
共 50 条
  • [1] Preparation of Indium Tin Oxide Sputtering Targets by Spark Plasma Sintering
    Guo Wei
    Wang Weimin
    Ma Xiuhua
    Jia Tiekun
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 407 - 410
  • [2] Sintering of a quasi-crystalline powder using spark plasma sintering and hot-pressing
    Ramond, Laure
    Bernard-Granger, Guillaume
    Addad, Ahmed
    Guizard, Christian
    ACTA MATERIALIA, 2010, 58 (15) : 5120 - 5128
  • [3] Rapid preparation of indium tin oxide sputtering targets by spark plasma sintering
    Takeuchi, T
    Ishida, T
    Ichikawa, K
    Miyamoto, S
    Kawahara, M
    Kageyama, H
    JOURNAL OF MATERIALS SCIENCE LETTERS, 2002, 21 (11) : 855 - 857
  • [4] Comparison of hot pressing and spark plasma sintering in the densification behavior of indium tin oxide-borosilicate glass composites
    Rudzik, Thomas J.
    Gerhardt, Rosario A.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2018, 101 (02) : 577 - 589
  • [5] AUTOMATED SINTERING AND HOT-PRESSING
    BECK, JH
    POWDER METALLURGY INTERNATIONAL, 1978, 10 (03): : 134 - 135
  • [6] Spark plasma sintering of a commercially available granulated zirconia powder: Comparison with hot-pressing
    Bernard-Granger, Guillaume
    Addad, Ahmed
    Fantozzi, Gilbert
    Bonnefont, Guillaume
    Guizard, Christian
    Vernat, Dorothee
    ACTA MATERIALIA, 2010, 58 (09) : 3390 - 3399
  • [7] HOT-PRESSING AND SINTERING OF TIN STAINLESS STEEL METALLURGICAL SYSTEM
    HARUSH, S
    ITZHAK, D
    POWDER METALLURGY, 1988, 31 (03) : 178 - 183
  • [8] Comparison of spark plasma sintering and hot pressing of MgAlON
    Huang, Qing
    Zhang, Houxing
    Huang, Yong
    Li, Haifeng
    Wan, Zhijian
    High-Performance Ceramics IV, Pts 1-3, 2007, 336-338 : 1060 - 1061
  • [9] Preparation of Indium-Zinc-Oxide Thin Film Transistors by Hot-Pressing Sintering Target
    Song Er-Long
    Lan Lin-Feng
    Lin Zhen-Guo
    Sun Sheng
    Song Wei
    Li Yu-Zhi
    Gao Pei-Xiong
    Zhang Peng
    Peng Jun-Biao
    ACTA PHYSICO-CHIMICA SINICA, 2017, 33 (10) : 2092 - 2098
  • [10] Consolidation of Carbon Nanofiber/Copper Composites by Hot-Pressing and Spark Plasma Sintering: A Comparative Study
    Barcena, Jorge
    Martinez, Vladimir
    Martinez, Ramon
    Maudes, Jon
    Sarries, Jose-Ignacio
    Caro, Inaki
    Gonzalez, Javier-Jesus
    Coleto, Javier
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2009, 9 (03) : 1797 - 1802
12345