Fatigue crack propagation behavior of Ni-based superalloys after overloading at elevated temperatures

被引：9

作者：

Huang, Xinyue ^{[1
]}

Wang, Liang ^{[1
]}

Hu, Yunming ^{[2
]}

Guo, Guangping ^{[1
]}

Salmon, David ^{[2
]}

Li, Ying ^{[1
]}

Zhao, Wenxia ^{[3
]}

机构：

[1] Beijing Inst Aeronaut Mat, Natl Key Lab Sci & Technol Adv High Temp Struct M, Beijing 100095, Peoples R China

[2] MTS Syst Corp, Eden Prairie, MN 55344 USA

[3] Beijing Inst Aeronaut Mat, Beijing Key Lab Aeronaut Mat Testing & Evaluat, Beijing 100095, Peoples R China

来源：

PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL | 2016年 / 26卷 / 02期

关键词：

High temperature fatigue; Fatigue crack propagation rate; Overloading; Crack closure; Superalloys; GROWTH; ALLOY;

D O I：

10.1016/j.pnsc.2016.03.007

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The fatigue crack propagation behavior of three superalloys subjected to a single overloading at elevated temperatures was investigated. The fatigue crack propagation rate FCPR versus stress intensity factor range data da/dN-Delta K were calculated using the two-point secant method. It was found that the crack growth rates of the investigated materials were retarded after overloading with an overload ratio R-OL = 1.6. The size of the plastic zone in the front of the crack tip and its relation to loading level were discussed. The overload retardation effects are attributed to crack closure. The fatigue damage in the plastic zone can also be a factor to explain the overload retardation. (C) 2016 Published by Chinese Materials Research Society.

引用

页码：197 / 203

页数：7

共 50 条

[31] REVIEW OF DEFECT BEHAVIOR IN Ni-BASED SUPERALLOYS
Campbell, John
SHAPE CASTING: 4TH INTERNATIONAL SYMPOSIUM 2011 IN HONOR OF PROF. JOHN T. BERRY, 2011, : 71 - 78
[32] Microstructural influences on fatigue crack initiation and early propagation in Ni-based superalloy
Kim, Donghyuk
Jiang, Rong
Sinclair, Ian
Reed, Philippa
MATERIALS SCIENCE AND TECHNOLOGY, 2022, 38 (14) : 1081 - 1094
[33] Crack initiation anisotropy of Ni-based SX superalloys in the very high cycle fatigue regime
Cervellon, Alice
Torbet, Chris J.
Pollock, Tresa M.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 825
[34] Time-Dependent Fatigue Crack Propagation Behavior of Two Solid-Solution-Strengthened Ni-Based Superalloys-INCONEL 617 and HAYNES 230
Ma, Longzhou
Roy, Shawoon K.
Hasan, Muhammad H.
Pal, Joydeep
Chatterjee, Sudin
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (02): : 491 - 504
[35] FATIGUE-CRACK PROPAGATION BEHAVIOR OF INCOLOY-800 AT ELEVATED-TEMPERATURES
JAMES, LA
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1974, 96 (04): : 249 - 254
[36] Oxidation accelerated dwell fatigue crack growth mechanisms of a coarse grained PM Ni-based superalloy at elevated temperatures
Wu, C. H.
Jiang, R.
Zhang, L. C.
Wang, Y. C.
Chen, Y.
Song, Y. D.
CORROSION SCIENCE, 2022, 209
[37] Fracture and fatigue behavior of sintered steel at elevated temperatures: Part II. Fatigue crack propagation
Zhaohui Shan
Yang Leng
Metallurgical and Materials Transactions A, 1999, 30 : 2895 - 2904
[38] Fracture and fatigue behavior of sintered steel at elevated temperatures: Part II. Fatigue crack propagation
Shan, ZH
Leng, Y
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (11): : 2895 - 2904
[39] Fatigue crack propagation after overloading and underloading at negative stress ratios
Silva, F. S.
INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (9-11) : 1757 - 1771
[40] MICROSTRUCTURE AND THERMOMECHANICAL FATIGUE BEHAVIOR OF DIRECTIONALLY SOLIDIFIED NI-BASED SUPERALLOYS IN OP CONDITION
Seo, Dongyi
Seo, Seong-Moon
Yoo, Young-Soo
Kim, Daejin
PROCEEDINGS OF THE ASME TURBO EXPO: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, 2018, VOL 6, 2018,

← 1 2 3 4 5 →