Fatigue crack propagation behavior of Ni-based superalloys after overloading at elevated temperatures

被引：9
|
作者：
Huang, Xinyue [1 ]
Wang, Liang [1 ]
Hu, Yunming [2 ]
Guo, Guangping [1 ]
Salmon, David [2 ]
Li, Ying [1 ]
Zhao, Wenxia [3 ]
机构：
[1] Beijing Inst Aeronaut Mat, Natl Key Lab Sci & Technol Adv High Temp Struct M, Beijing 100095, Peoples R China
[2] MTS Syst Corp, Eden Prairie, MN 55344 USA
[3] Beijing Inst Aeronaut Mat, Beijing Key Lab Aeronaut Mat Testing & Evaluat, Beijing 100095, Peoples R China
来源：
PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL | 2016年 / 26卷 / 02期
关键词：
High temperature fatigue; Fatigue crack propagation rate; Overloading; Crack closure; Superalloys; GROWTH; ALLOY;
D O I：
10.1016/j.pnsc.2016.03.007
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fatigue crack propagation behavior of three superalloys subjected to a single overloading at elevated temperatures was investigated. The fatigue crack propagation rate FCPR versus stress intensity factor range data da/dN-Delta K were calculated using the two-point secant method. It was found that the crack growth rates of the investigated materials were retarded after overloading with an overload ratio R-OL = 1.6. The size of the plastic zone in the front of the crack tip and its relation to loading level were discussed. The overload retardation effects are attributed to crack closure. The fatigue damage in the plastic zone can also be a factor to explain the overload retardation. (C) 2016 Published by Chinese Materials Research Society.
引用
收藏
页码：197 / 203
页数：7
相关论文
共 50 条
  • [1] Fatigue crack propagation behavior of Ni-based superalloys after overloading at elevated temperatures
    Xinyue Huang
    Liang Wang
    Yunming Hu
    Guangping Guo
    David Salmon
    Ying Li
    Wenxia Zhao
    Progress in Natural Science:Materials International, 2016, 26 (02) : 197 - 203
  • [2] Effect of load ratio on fatigue crack propagation behavior of solid-solution-strengthened Ni-based superalloys at elevated temperature
    Ma, Longzhou
    Roy, Shawoon K.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 435 (1-3) : 88 - 95
  • [3] Subsurface crack formation and propagation of fretting fatigue in Ni-based single-crystal superalloys
    Han, Qi-Nan
    Rui, Shao-Shi
    Qiu, Wenhui
    Su, Yue
    Ma, Xianfeng
    He, Zhiwu
    Cui, Haitao
    Zhang, Hongjian
    Shi, Hui-Ji
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (11) : 2520 - 2532
  • [4] Toward Predictive Understanding of Fatigue Crack Nucleation in Ni-Based Superalloys
    Jiang, Jun
    Dunne, Fionn P. E.
    Ben Britton, T.
    JOM, 2017, 69 (05) : 863 - 871
  • [5] Toward Predictive Understanding of Fatigue Crack Nucleation in Ni-Based Superalloys
    Jun Jiang
    Fionn P. E. Dunne
    T. Ben Britton
    JOM, 2017, 69 : 863 - 871
  • [6] Mechanistic Modeling of Cyclic Softening in Ni-Based Superalloys at Elevated Temperatures
    Kwai S. Chan
    Metallurgical and Materials Transactions A, 2023, 54 : 106 - 120
  • [7] Mechanistic Modeling of Cyclic Softening in Ni-Based Superalloys at Elevated Temperatures
    Chan, Kwai S.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2023, 54 (01): : 106 - 120
  • [8] Fatigue crack growth in nickel-based superalloys at elevated temperatures
    Abbadi, M.
    Hahner, P.
    Belouettar, S.
    Zenasni, M.
    MATERIALS & DESIGN, 2011, 32 (05): : 2710 - 2716
  • [9] Fatigue behavior in monocrystalline Ni-based superalloys for blade applications
    Yablinsky, C. A.
    Flores, K. M.
    Mills, M. J.
    Williams, J. C.
    Rigney, Joe
    SUPERALLOYS 2008, 2008, : 535 - +
  • [10] Acceleration mechanism of the degradation of the lifetime of Ni-based superalloys under creep-fatigue loading at elevated temperatures
    Luo, Yifan
    Takahashi, Yukako
    Nakayama, Koki
    Nakayama, Ayumi
    Suzuki, Ken
    Miura, Hideo
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2023, 46 (08) : 3043 - 3059
12345