Interaction of silty sand and preformed corrosion products on N80 carbon steel in CO2 environment

被引：11

作者：

Chen, Longjun ^{[1
]}

Liu, Wei ^{[1
]}

Zhang, Tianyi ^{[1
]}

Dong, Baojun ^{[1
]}

Li, Hai ^{[1
]}

Sun, Yipu ^{[1
]}

Fan, Yueming ^{[1
]}

Zhao, Yonggang ^{[1
]}

Li, Wenqi ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Corros & Protect Ctr, Beijing 100083, Peoples R China

来源：

CORROSION SCIENCE | 2022年 / 205卷

基金：

中国国家自然科学基金;

关键词：

Carbon steel; CO2; corrosion; Silty sand; Iron carbonate; Antagonism effect; EROSION-CORROSION; MILD-STEEL; PERFORMANCE; MECHANISM; BEHAVIOR; OIL; FILM; X65;

D O I：

10.1016/j.corsci.2022.110467

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The interaction of silty sand and corrosion products layer in sweet environment was evaluated. Corrosion protection was a function of two factors, i.e., adsorption and embedment of silty sand, and the presence of corrosion products layer. Silty sand could block ions transportation and slow down the dissolution of FeCO3. The main protection was offered by corrosion products, this effect was more significant in the presence of a full coverage FeCO3 layer. FeCO3-rich layer not only prevented the embedment of silty sand but also reduced the adsorption. Silty sand and corrosion products layer exhibited an obvious antagonism effect.

引用

页数：19

共 50 条

[21] Inhibition of CO2 corrosion of N80 carbon steel by carboxylic quaternary imidazoline and halide ions additives
P. C. Okafor
C. B. Liu
X. Liu
Y. G. Zheng
Journal of Applied Electrochemistry, 2009, 39 : 2535 - 2543
[22] Inhibition of CO2 corrosion of N80 carbon steel by carboxylic quaternary imidazoline and halide ions additives
Okafor, P. C.
Liu, C. B.
Liu, X.
Zheng, Y. G.
JOURNAL OF APPLIED ELECTROCHEMISTRY, 2009, 39 (12) : 2535 - 2543
[23] Characteristics of CO2 corrosion scale formed on N80 steel in stratum water with saturated CO2
Li, D. G.
Feng, Y. R.
Bai, Z. Q.
Zheng, M. S.
APPLIED SURFACE SCIENCE, 2007, 253 (20) : 8371 - 8376
[24] Effect of calcium ions on pitting corrosion and inhibition performance in CO2 corrosion of N80 steel
Jiang, X.
Zheng, Y. G.
Qu, D. R.
Ke, W.
CORROSION SCIENCE, 2006, 48 (10) : 3091 - 3108
[25] Evaluation of Carbon Dioxide Corrosion on N80 Steel
Fan, Zhenzhong
Tong, Anqi
Cui, Yan
Yang, Junfeng
MECHANICAL DESIGN AND POWER ENGINEERING, PTS 1 AND 2, 2014, 490-491 : 311 - +
[26] Role of polyacrylamide concentration on corrosion behavior of N80 steel in the HPAM/H2S/CO2 environment
Dong, Baojun
Zeng, Dezhi
Yu, Zhiming
Zhang, Haixin
Yu, Huiyong
Tian, Gang
Yi, Yonggang
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2020, 71 (04): : 526 - 536
[27] Novel Сarbon Dots for Corrosion Inhibition of N80 Carbon Steel in 3% Saturated CO2 Saline Solution
Xiaodan Wu
Jianbo Li
Jie Lv
Chaoyi Deng
Lan Yang
Russian Journal of Applied Chemistry, 2021, 94 : 1111 - 1121
[28] N80 Oil Tube Steel Corrosion Behavior in Different CO2 Saturated Brine
Ma, Yun
Zhang, Qingbo
Bai, Haitao
EKOLOJI, 2018, 27 (106): : 113 - 121
[29] Macrocyclic inhibitor for corrosion of N80 steel in 3.5% NaCl solution saturated with CO2
Singh, Ambrish
Lin, Yuanhua
Obot, I. B.
Ebenso, Eno E.
JOURNAL OF MOLECULAR LIQUIDS, 2016, 219 : 865 - 874
[30] Investigation on CO2 corrosion Behaviors of N80 tubing steel under stress conditions
Li Dang-Guo
Feng Yao-Rong
Bai Zhen-Quan
Zhen Mao-Sheng
ACTA CHIMICA SINICA, 2007, 65 (17) : 1807 - 1813

← 1 2 3 4 5 →