Mechanical Properties of Fragrant Screwpine Fiber Reinforced Unsaturated Polyester Composite: Effect of Fiber Length, Fiber Treatment and Water Absorption

Fragrant screwpine fiber reinforced unsaturated polyester composites (FSFRUPC) were subjected to water immersion tests in order to examine the effect of water absorption on the mechanical properties. FSFRUP composite specimen containing 30 % fiber volume fraction with fiber length of 3 mm and 9 mm was considered in this study. Water absorption test was performed by immersing specimen in sea, distilled and well water at room temperature under different time durations (24, 48, 72, 96, 120, 144, 168, 192, 216, 240 hours). The tensile, flexural and impact properties of the water absorption specimen were appraised and compared with those of the dry composite specimen as per the ASTM standard. The tensile, flexural and impact properties of FSFRUPC specimen were found to decrease with the increase in the percentage of moisture uptake. The percentage of moisture uptake of composite was reduced after alkali treatment with 3 % NaoH for 3 hours. In moisture absorption test, the lowest diffusion coefficient, D (6.62513x10(-13) m(2)/s) and swelling rate parameter, K-sr (6.341x10(-3)h(-1)) were obtained through the specimen immersed in sea water. The chemical composition, elemental composition of fiber and surface morphology of the FSFRUPC were analysed by using Fourier transform infrared spectroscopy (FTIR), Energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM) respectively.