Inhibition of CO2 corrosion of N80 carbon steel by carboxylic quaternary imidazoline and halide ions additives

被引：41
|
作者：
Okafor, P. C. [1 ,2 ]
Liu, C. B. [1 ]
Liu, X. [1 ,3 ]
Zheng, Y. G. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Liaoning, Peoples R China
[2] Univ Calabar, Dept Pure & Appl Chem, Calabar, Nigeria
[3] Shenyang Inst Chem Technol, Dept Appl Chem, Shenyang 110142, Peoples R China
来源：
JOURNAL OF APPLIED ELECTROCHEMISTRY | 2009年 / 39卷 / 12期
关键词：
CO2; corrosion; Mild steel; Imidazoline; Halide ions; Synergism; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; 3-PERCENT NACL SOLUTION; MILD-STEEL; DIOXIDE CORROSION; ANODIC-DISSOLUTION; SULFURIC-ACID; HYDROCHLORIC-ACID; H2SO4; SOLUTIONS; REACTION MODEL; IRON;
D O I：
10.1007/s10800-009-9948-5
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The inhibition of the corrosion of N80 mild steel by 2-undecyl-1-1-ethylamino-1-ethylcarboxyl quaternary imidazoline (CQI) in CO2-saturated 3% NaCl and 3% Na2SO4 solutions was studied using electrochemical methods. Inhibition efficiency increased with increase in CQI concentration and synergistically increased in the presence of halide ions. CQI inhibited the corrosion reaction by chemical adsorption on the metal/solution interface in halide free solutions and by a combination of chemical and coulombic attraction in the presence of halide ions. The adsorption characteristics of the inhibitor were approximated by Frumkin isotherm and El-Awady et al. kinetic-thermodynamic model.
引用
收藏
页码：2535 / 2543
页数：9
相关论文
共 50 条
  • [31] CORROSION AND INHIBITION STUDY OF API N-80 CARBON STEEL IN CO2 ENVIRONMENT.
    Su, Chun-Chi
    Oung, Jung-Chou
    Wu, Jou Y.
    1600, (01):
  • [32] Investigation of Individual and Synergistic Effects of Salinity and Temperature on CO2 Corrosion Performance of Low Carbon API N80 Steel
    Hoomehr, B.
    Pakshir, M.
    Rahsepar, M.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (10) : 4643 - 4654
  • [33] Investigation of Individual and Synergistic Effects of Salinity and Temperature on CO2 Corrosion Performance of Low Carbon API N80 Steel
    B. Hoomehr
    M. Pakshir
    M. Rahsepar
    Journal of Materials Engineering and Performance, 2023, 32 : 4643 - 4654
  • [34] Effect and Mechanism of Temperature on the Corrosion Behavior of N80 Steel in Simulated Formation with Saturated CO2
    Liu, Wan-Ying
    Li, Jin-Yu
    Gao, Ke-Chao
    Zhang, Zhi
    Shang, Suo-Gui
    Gao, Qiang-Yong
    Ma, Jin-Xin
    Surface Technology, 2022, 51 (08): : 353 - 362
  • [35] Corrosion of N80 carbon steel in oil field formation water containing CO2 in the absence and presence of acetic acid
    Zhu, S. D.
    Fu, A. Q.
    Miao, J.
    Yin, Z. F.
    Zhou, G. S.
    Wei, J. F.
    CORROSION SCIENCE, 2011, 53 (10) : 3156 - 3165
  • [36] Unveiling the influential mechanism of O2 on the corrosion of N80 carbon steel under dynamic supercritical CO2 conditions
    Li, Y. Y.
    Jiang, Z. N.
    Zhang, Q. H.
    Lei, Y.
    Wang, X.
    Zhang, G. A.
    CORROSION SCIENCE, 2022, 205
  • [37] Influence of CO2 partial pressure on the protection property of corrosion scale formed on N80 steel
    Chen, Dong
    Liu, Wei
    Lu, Minxu
    Wu, Yinshun
    Hou, Shiying
    Chen, Yingfeng
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2007, 29 (03): : 288 - 292
  • [38] Influence of H2S Content on CO2 Corrosion Behaviors of N80 Tubing Steel
    Jingen, D.
    Wei, Y.
    Xiaorong, L.
    Xiaoqin, D.
    PETROLEUM SCIENCE AND TECHNOLOGY, 2011, 29 (13) : 1387 - 1396
  • [39] The influence of Ca2+ on the growth mechanism of corrosion product film on N80 steel in CO2 corrosion environments
    Ren, Xiedong
    Lu, Yuan
    Wei, Qiang
    Yu, Liusi
    Zhai, Kaiyuan
    Tang, Jiayi
    Wang, Hu
    Xie, Juan
    CORROSION SCIENCE, 2023, 218
  • [40] Corrosion inhibition of N80 steel in hydrochloric acid by phenol derivatives
    Vishwanatham, S.
    Haldar, Nilesh
    INDIAN JOURNAL OF CHEMICAL TECHNOLOGY, 2007, 14 (05) : 501 - 506
12345