Grain refinement mechanism in A3003 alloy

In the present study, in order to find out an grain refinement mechanism, 0.1wt.% Al-10wt.%Ti master alloy was added into A3003 alloy melt contained in graphite crucible and in alumina crucible, and then the melt holding time at 750 degrees C was systematically changed from 1 min up to 120 min. It is interesting to note that the grain refinement and fading phenomena remarkably depend on the crucible material. The fading effect in the specimens using alumina crucible can be explained as the result of TiAl(3) phase dissolution into molten aluminium matrix. In the specimens using graphite crucible, the grain refinement was occurred gradually with increasing holding time. It was suggest that the continuous grain refinement is due to transition of refinement mechanism from TiAl(3) phase to TiC phase. It can be mentioned that the TiC formed from titanium and carbon solute in the aluminium melt, which came from the Al-10Ti alloy and the graphite crucible.