Hot Compressive Deformation Behavior and Constitutive Equation of Al-9.39Zn-1.92Mg-1.98Cu Alloy

被引:0
|
作者
Shi Guohui [1 ]
Zhang Yongan [1 ]
Li Xiwu [1 ]
Li Zhihui [1 ]
Yan Lizhen [1 ]
Yan Hongwei [1 ]
Liu Hongwei [1 ]
Xiong Baiqing [1 ,2 ]
机构
[1] GRIMAT Engn Inst Co Ltd, State Key Lab Nonferrous Met & Proc, Beijing 101407, Peoples R China
[2] GRINM Grp Co Ltd, Beijing 100088, Peoples R China
关键词
Al-Zn-Mg-Cu alloys; hot compressive deformation; flow stress behavior; constitutive equation model; 7050; ALUMINUM-ALLOY; MICROSTRUCTURAL EVOLUTION; FLOW BEHAVIOR; SUPERALLOY;
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Hot compression tests for the Al-9.39Zn-1.92Mg-1.98Cu alloy were carried out at the temperature ranging from 300 degrees C to 460 degrees C and the strain rate ranging from 0.001 s(-1) to 1 s(-1), and the height reduction degree was 70%. The flow stress was corrected because of the effect of friction. Results show the flow stress decreases with increasing the temperature or decreasing the strain rate. The friction effect becomes more and more obvious with increasing the temperature and decreasing the strain rate. A revised constitutive equation considering the influence of strain is established based on the Arrhenius-type model. Comparing the experimental and predicted flow stresses, the revised constitutive equation has higher accuracy. Their correlation coefficient and average absolute relative error is 0.996 and 2.45%, respectively.
引用
收藏
页码:2753 / 2758
页数:6
相关论文
共 50 条
  • [21] Investigation into Constitutive Equation and Hot Compression Deformation Behavior of 6061 Al Alloy
    Zhang, Xiang
    Wang, Xiaoxi
    Zhang, Dekun
    TEHNICKI VJESNIK-TECHNICAL GAZETTE, 2019, 26 (05): : 1376 - 1382
  • [22] Hot Deformation Behavior and Microstructure Evolution of a Novel Al-Zn-Mg-Li-Cu Alloy
    Wu, Shuaishuai
    Zhu, Baohong
    Jiang, Wei
    Qiu, Haochen
    Guo, Yang
    MATERIALS, 2022, 15 (19)
  • [23] Hot deformation behavior of Al-Cu-Li-Mg-Zr alloy containing Zn and Mn
    Chen Yong-lai
    Li Jin-feng
    Lue Hong-jun
    Li Shi-chen
    Zheng Zi-qiao
    Zhang Yu-wei
    Zhang Xu-hu
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 : S271 - S275
  • [24] Hot deformation behavior of Al-Cu-Li-Mg-Zr alloy containing Zn and Mn
    陈永来
    李劲风
    吕宏军
    李世晨
    郑子樵
    张宇伟
    张绪虎
    Transactions of Nonferrous Metals Society of China, 2007, (S1) : 271 - 275
  • [25] Microstructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation
    Shi, Cangji
    Lai, Jing
    Chen, X. -Grant
    MATERIALS, 2014, 7 (01): : 244 - 264
  • [26] Constitutive Analysis and Hot Deformation Behavior of Homogenized Al-3Mg Alloy
    P. M. Keshtiban
    F. Bashirzadeh
    JOM, 2023, 75 : 905 - 913
  • [27] Constitutive Analysis and Hot Deformation Behavior of Homogenized Al-3Mg Alloy
    Keshtiban, P. M.
    Bashirzadeh, F.
    JOM, 2023, 75 (03) : 905 - 913
  • [28] Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy
    Cai, Jun
    Chen, Lin
    Yang, Juan
    Wang, Wen
    Ding, Ben
    Yang, Qingxiang
    Qiao, Ke
    Wang, Kuaishe
    METALS, 2022, 12 (10)
  • [29] Hot Deformation Behavior Considering Strain Effects and Recrystallization Mechanism of an Al-Zn-Mg-Cu Alloy
    Luo, Lei
    Liu, Zhiyi
    Bai, Song
    Zhao, Juangang
    Zeng, Diping
    Wang, Jian
    Cao, Jing
    Hu, Yangcheng
    MATERIALS, 2020, 13 (07)
  • [30] Study on hot deformation behavior and dynamic recrystallization mechanism of recycled Al-Zn-Mg-Cu alloy
    Qin, Chuan-guang
    Jiang, Bo
    Hu, Mao-liang
    Wang, Ye
    Xu, Hong-yu
    Guo, Yu
    Ji, Ze-sheng
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 33 : 4725 - 4738