Electrochemical corrosion behavior of bronze materials in an acid-containing simulated atmospheric environment

被引：11

作者：

Cai, Lankun ^{[1
]}

Chen, Mengjie ^{[1
]}

Wang, Ying ^{[1
]}

Chen, Cheng ^{[1
]}

Zhang, Lehua ^{[1
,2
]}

Zhou, Hao ^{[3
]}

Wu, Laiming ^{[3
]}

Yan, Ying ^{[1
]}

机构：

[1] East China Univ Sci & Technol, State Environm Protect Key Lab Environm Risk Asse, Coll Resources & Environm Engn, Shanghai 200237, Peoples R China

[2] Shanghai Inst Pollut Control & Ecol Secur, Shanghai, Peoples R China

[3] Shanghai Museum, Shanghai, Peoples R China

来源：

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2020年 / 71卷 / 03期

关键词：

acetic acid; bronze; corrosion; formic acid; thin electrolyte layers; ACETIC-ACID; IMPEDANCE SPECTROSCOPY; COPPER; MAGNESIUM; STEEL; ALLOY; DC;

D O I：

10.1002/maco.201911196

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The present work investigates the corrosion behavior of bronze materials under thin electrolyte layers (TELs) in a simulated atmospheric environment containing formic and acetic acid by electrochemical measurements as well as surface characterization. The results show that the corrosion of bronze under TEL is significantly faster than that in the bulk solution, and the corrosion rate of bronze is the highest when the thickness of TEL is about 100 mu m. Formic acid is observed to be more corrosive than acetic acid. Copper formate and copper acetate hydrate appear in the corrosion products formed on the surface of bronze, suggesting that the organic acid participates in the corrosion process of bronze materials in the simulated atmospheric environment.

引用

页码：464 / 473

页数：10

共 50 条

[21] Hydrogen permeation behavior of scratch formed on Zn coated steels in simulated atmospheric corrosion environment
Kei S.
Masatoshi S.
Junichiro K.
ISIJ International, 2021, 61 (04) : 1120 - 1126
[22] Wavelet Analysis of Electrochemical Noise Measurements During Atmospheric Corrosion of Mild Steel in the Simulated Marine Environment
Dang, Lihua
Gao, Zhiming
Wang, Xinyue
Wei, Chen
Han, Lianheng
Chen, Jianguo
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (05): : 4326 - 4337
[23] THE CORROSION OF MILD-STEEL IN ACETIC ACID-CONTAINING ATMOSPHERES
ALVES, HCD
FERREIRA, MGS
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1992, 340 (1-2) : 137 - 144
[24] Corrosion behavior of three bipolar plate materials in simulated SPE water electrolysis environment
Wang, Jun-Tao
Wang, Wei-Wei
Wang, Cheng
Mao, Zong-Qiang
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2012, 37 (17) : 12069 - 12073
[25] Effect of Mo on the Corrosion Resistance of Cr-Containing Steel in a Simulated Tropical Marine Atmospheric Environment
Wang, Ningxi
Gao, Jianzhuo
Xu, Xuexu
CRYSTALS, 2024, 14 (02)
[26] In-situ investigation of atmospheric corrosion behavior of bronze under thin electrolyte layers using electrochemical technique
Liao Xiao-ning
Cao Fa-he
Chen An-na
Liu Wen-juan
Zhang Jian-qing
Cao Chu-nan
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (05) : 1239 - 1249
[27] MONITORING ATMOSPHERIC CORROSION WITH ELECTROCHEMICAL METHODS IN LABORATORY ENVIRONMENT
METIKOSHUKOVIC, M
ZEVNIK, C
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1984, 35 (03): : 116 - 120
[28] Scaling and electrochemical corrosion behavior of 304 stainless steel pipes in a simulated geothermal water environment
Wu, Kun-Hu
Li, Wei-Ping
Liu, Hui-Cong
Zhu, Li-Qun
Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2009, 31 (10): : 1263 - 1269
[29] Study on electrochemical behavior of 690 alloy with corrosion products in simulated PWR primary water environment
Cheng, Xuequn
Zuo, Xiao Mei
ANTI-CORROSION METHODS AND MATERIALS, 2018, 65 (06) : 616 - 625
[30] Corrosion testing of materials in simulated superheated geothermal environment
Thorhallsson, Andri Isak
Stefansson, Andri
Kovalov, Danyil
Karlsdottir, Sigrun Nanna
CORROSION SCIENCE, 2020, 168 (168)

← 1 2 3 4 5 →